IS 11169 (Part 1) 15Ni5Cr5 vs IS 11169 (Part 1) 30Ni13Cr5

Close Alternative — 84.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 15Ni5Cr5 (IS 11169 (Part 1):2022) and IS 11169 (Part 1) 30Ni13Cr5 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 15Ni5Cr5 is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while IS 11169 (Part 1) 30Ni13Cr5 is commonly used for heavy shafts, axles, connecting rods, large gears, structural components in mining and construction equipment.. IS 11169 (Part 1) 15Ni5Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 30Ni13Cr5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 15Ni5Cr5 vs IS 11169 (Part 1) 30Ni13Cr5 is a 84% match. As per mechanical properties, the match is 100%. Combined, this makes them a close alternative overall at 84.9%.

Frequently Compared With IS 11169 (Part 1) 15Ni5Cr5:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
84%
MECHANICAL MATCH
100%
OVERALL
84.9%
Specifications
Property IS 11169 (Part 1) 15Ni5Cr5 IS 11169 (Part 1) 30Ni13Cr5
Standard IS 11169 (Part 1):2022 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.26-0.34
Cr (%) 1.00-1.40 1.10-1.40
Cu (%) <=0.15 Not specified
Mn (%) 0.40-0.70 0.40-0.70
Mo (%) <=0.05 Not specified
Ni (%) 3.80-4.30 3.90-4.30
P (%) <=0.035 Not specified
S (%) <=0.035 Not specified
Si (%) 0.10-0.35 0.10-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 15Ni5Cr5 IS 11169 (Part 1) 30Ni13Cr5
Hardness, annealed (+AC) <=200 HBW Not specified
Hardness, annealed Not specified <=200 HB
Typical Applications
IS 11169 (Part 1) 15Ni5Cr5
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
IS 11169 (Part 1) 30Ni13Cr5
Heavy shafts, axles, connecting rods, large gears, structural components in mining and construction equipment.
Key Differences
Can IS 11169 (Part 1) 15Ni5Cr5 Be Substituted With IS 11169 (Part 1) 30Ni13Cr5?
IS 11169 (Part 1) 15Ni5Cr5 and IS 11169 (Part 1) 30Ni13Cr5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
Forms & Sizes Available on M-EX
IS 11169 (Part 1) 15Ni5Cr5
No active listings currently.
IS 11169 (Part 1) 30Ni13Cr5
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4800–5900 mm (188.98–232.28 in)
On M-EX Right Now
IS 11169 (Part 1) 15Ni5Cr5
0 active listings and RFQs →
IS 11169 (Part 1) 30Ni13Cr5
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 15Ni5Cr5 and IS 11169 (Part 1) 30Ni13Cr5?
IS 11169 (Part 1) 15Ni5Cr5 specifies Cu, Mo, P, S which are not specified for IS 11169 (Part 1) 30Ni13Cr5.
Can IS 11169 (Part 1) 15Ni5Cr5 be substituted with IS 11169 (Part 1) 30Ni13Cr5?
IS 11169 (Part 1) 15Ni5Cr5 and IS 11169 (Part 1) 30Ni13Cr5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.