IS 11169 (Part 1) 17C10BT vs UNI 11234 100Cr6

Minimal Match — 44.2% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 17C10BT (IS 11169 (Part 1):2022) and UNI 11234 100Cr6 (UNI 11234:2007) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 17C10BT is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while UNI 11234 100Cr6 is commonly used for ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components. IS 11169 (Part 1) 17C10BT is defined under Bureau of Indian Standards (IS), originating from India, while UNI 11234 100Cr6 is defined under Ente Nazionale Italiano di Unificazione (UNI), originating from Italy.

As per chemical composition, IS 11169 (Part 1) 17C10BT vs UNI 11234 100Cr6 is a 66.4% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 44.2%.

Frequently Compared With IS 11169 (Part 1) 17C10BT:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 105Cr5 IS 11169 (Part 1) 10Ni5Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
66.4%
MECHANICAL MATCH
0%
OVERALL
44.2%
Specifications
Property IS 11169 (Part 1) 17C10BT UNI 11234 100Cr6
Standard IS 11169 (Part 1):2022 UNI 11234:2007
Category Alloy Steel Alloy Steel
B (%) 0.0008-0.005 Not specified
C (%) 0.15-0.20 0.93-1.05
Cr (%) <=0.30 1.35-1.65
Cu (%) <=0.25 Not specified
Mn (%) 0.90-1.20 0.25-0.45
P (%) <=0.025 <=0.025
S (%) <=0.025 <=0.025
Si (%) <=0.30 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 17C10BT UNI 11234 100Cr6
Core Hardness (CH) >=37 HRC up to 12 mm Not specified
Tensile Strength, annealed (+AC) <=480 MPa (over 5 to 25 mm) Not specified
Tensile Strength Not specified 750-1000 MPa
Yield Strength Not specified 400-600 MPa
Elongation Not specified 10-14 %
Hardness Not specified 60-64 HRC
Typical Applications
IS 11169 (Part 1) 17C10BT
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
UNI 11234 100Cr6
ball bearings,roller bearings,needle bearings,dies,punches,gauges,wear resistant components
Key Differences
Can IS 11169 (Part 1) 17C10BT Be Substituted With UNI 11234 100Cr6?
IS 11169 (Part 1) 17C10BT and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 11169 (Part 1) 17C10BT
No active listings currently.
UNI 11234 100Cr6
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5700–6800 mm (224.41–267.72 in)
On M-EX Right Now
IS 11169 (Part 1) 17C10BT
0 active listings and RFQs →
UNI 11234 100Cr6
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 17C10BT and UNI 11234 100Cr6?
IS 11169 (Part 1) 17C10BT specifies B, Cu which are not specified for UNI 11234 100Cr6.
Can IS 11169 (Part 1) 17C10BT be substituted with UNI 11234 100Cr6?
IS 11169 (Part 1) 17C10BT and UNI 11234 100Cr6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.