IS 11169 (Part 1) 17C8GC (case hardening) vs BS 970 (Part 1) 055M15

Minimal Match — 52.5% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 17C8GC (case hardening) (IS 11169 (Part 1):2022) and BS 970 (Part 1) 055M15 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Carbon Steel category. IS 11169 (Part 1) 17C8GC (case hardening) is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while BS 970 (Part 1) 055M15 is commonly used for as-rolled, or as-rolled and softened, steel (section two). IS 11169 (Part 1) 17C8GC (case hardening) is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 055M15 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 17C8GC (case hardening) vs BS 970 (Part 1) 055M15 is a 78.8% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 52.5%.

Frequently Compared With IS 11169 (Part 1) 17C8GC (case hardening):
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 080A20 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12
Match Breakdown
CHEMISTRY MATCH
78.8%
MECHANICAL MATCH
0%
OVERALL
52.5%
Specifications
Property IS 11169 (Part 1) 17C8GC (case hardening) BS 970 (Part 1) 055M15
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1991
Category Carbon Steel Carbon Steel
C (%) 0.15-0.19 <=0.20
Cu (%) <=0.25 Not specified
Mn (%) 0.60-0.90 <=0.80
P (%) <=0.025 Not specified
S (%) <=0.025 Not specified
Si (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 17C8GC (case hardening) BS 970 (Part 1) 055M15
Tensile Strength, as rolled (+AR) <=530 MPa (over 5 to 100 mm) Not specified
Condition Not specified As-rolled
Tensile Strength Not specified 310 MPa min
Elongation Not specified 25 % min
Hardness Not specified 121 HB min
Typical Applications
IS 11169 (Part 1) 17C8GC (case hardening)
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
BS 970 (Part 1) 055M15
As-rolled, or as-rolled and softened, steel (section two)
Key Differences
Can IS 11169 (Part 1) 17C8GC (case hardening) Be Substituted With BS 970 (Part 1) 055M15?
IS 11169 (Part 1) 17C8GC (case hardening) and BS 970 (Part 1) 055M15 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 17C8GC (case hardening)
0 active listings and RFQs →
BS 970 (Part 1) 055M15
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 17C8GC (case hardening) and BS 970 (Part 1) 055M15?
IS 11169 (Part 1) 17C8GC (case hardening) specifies Cu, P, S, Si which are not specified for BS 970 (Part 1) 055M15.
Can IS 11169 (Part 1) 17C8GC (case hardening) be substituted with BS 970 (Part 1) 055M15?
IS 11169 (Part 1) 17C8GC (case hardening) and BS 970 (Part 1) 055M15 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.