IS 11169 (Part 1) 17Ni2Cr2Mo2 vs AISI 8615

Strong Match — 92.2% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 17Ni2Cr2Mo2 (IS 11169 (Part 1):2022) and AISI 8615 are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 17Ni2Cr2Mo2 is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while AISI 8615 is commonly used for used for gears, shafts, pinions, bushings, transmission parts, and carburized machinery components.. IS 11169 (Part 1) 17Ni2Cr2Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while AISI 8615 is defined under AISI, originating from United States.

As per chemical composition, IS 11169 (Part 1) 17Ni2Cr2Mo2 vs AISI 8615 is a 92.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 92.2%.

Frequently Compared With IS 11169 (Part 1) 17Ni2Cr2Mo2:
IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 UNI 11234 100Cr6 IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
92.2%
MECHANICAL MATCH
No shared data
OVERALL
92.2%
Specifications
Property IS 11169 (Part 1) 17Ni2Cr2Mo2 AISI 8615
Standard IS 11169 (Part 1):2022 AISI
Category Alloy Steel Alloy Steel
C (%) 0.15-0.20 0.13-0.18
Cr (%) 0.40-0.60 0.40-0.60
Cu (%) <=0.35 Not specified
Mn (%) 0.70-0.90 0.70-0.90
Mo (%) 0.15-0.25 0.15-0.25
Ni (%) 0.40-0.70 0.40-0.70
P (%) <=0.030 0.035 max
S (%) <=0.040 0.040 max
Si (%) 0.15-0.35 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 17Ni2Cr2Mo2 AISI 8615
Tensile Strength Not specified 700-900 MPa
Yield Strength Not specified 500-700 MPa
Elongation Not specified 14-20%
Hardness Not specified 180-240 HB
Typical Applications
IS 11169 (Part 1) 17Ni2Cr2Mo2
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
AISI 8615
Used for gears, shafts, pinions, bushings, transmission parts, and carburized machinery components.
Key Differences
Can IS 11169 (Part 1) 17Ni2Cr2Mo2 Be Substituted With AISI 8615?
IS 11169 (Part 1) 17Ni2Cr2Mo2 and AISI 8615 overlap closely enough on chemistry and mechanical properties that AISI 8615 is often considered as a substitute for IS 11169 (Part 1) 17Ni2Cr2Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 11169 (Part 1) 17Ni2Cr2Mo2
No active listings currently.
AISI 8615
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4900–6300 mm (192.91–248.03 in)
On M-EX Right Now
IS 11169 (Part 1) 17Ni2Cr2Mo2
0 active listings and RFQs →
AISI 8615
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 17Ni2Cr2Mo2 and AISI 8615?
IS 11169 (Part 1) 17Ni2Cr2Mo2 specifies Cu which is not specified for AISI 8615.
Can IS 11169 (Part 1) 17Ni2Cr2Mo2 be substituted with AISI 8615?
IS 11169 (Part 1) 17Ni2Cr2Mo2 and AISI 8615 overlap closely enough on chemistry and mechanical properties that AISI 8615 is often considered as a substitute for IS 11169 (Part 1) 17Ni2Cr2Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.