IS 11169 (Part 1) 20Mn5Cr5S3 vs BS 970 (Part 1) 590H17

Close Alternative — 75.6% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 20Mn5Cr5S3 (IS 11169 (Part 1):2022) and BS 970 (Part 1) 590H17 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 20Mn5Cr5S3 is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while BS 970 (Part 1) 590H17 is commonly used for case hardening steel supplied to specified hardenability limits (end quench test, table 10).. IS 11169 (Part 1) 20Mn5Cr5S3 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 590H17 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 20Mn5Cr5S3 vs BS 970 (Part 1) 590H17 is a 75.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 75.6%.

Frequently Compared With IS 11169 (Part 1) 20Mn5Cr5S3:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6
Match Breakdown
CHEMISTRY MATCH
75.6%
MECHANICAL MATCH
No shared data
OVERALL
75.6%
Specifications
Property IS 11169 (Part 1) 20Mn5Cr5S3 BS 970 (Part 1) 590H17
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.17-0.22 0.14-0.20
Cr (%) 1.00-1.30 0.80-1.10
Cu (%) <=0.25 Not specified
Mn (%) 1.10-1.40 1.00-1.30
P (%) <=0.025 <=0.035
S (%) 0.020-0.040 <=0.040
Si (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 20Mn5Cr5S3 BS 970 (Part 1) 590H17
Hardness, ferrite-pearlite (+FP) 152-201 HB Not specified
Tensile Strength, annealed (+AC) <=570 MPa (over 5 to 40 mm) Not specified
Typical Applications
IS 11169 (Part 1) 20Mn5Cr5S3
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
BS 970 (Part 1) 590H17
Case hardening steel supplied to specified hardenability limits (end quench test, Table 10).
Key Differences
Can IS 11169 (Part 1) 20Mn5Cr5S3 Be Substituted With BS 970 (Part 1) 590H17?
IS 11169 (Part 1) 20Mn5Cr5S3 and BS 970 (Part 1) 590H17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 1) 20Mn5Cr5S3
0 active listings and RFQs →
BS 970 (Part 1) 590H17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 20Mn5Cr5S3 and BS 970 (Part 1) 590H17?
IS 11169 (Part 1) 20Mn5Cr5S3 specifies Cu, Si which are not specified for BS 970 (Part 1) 590H17.
Can IS 11169 (Part 1) 20Mn5Cr5S3 be substituted with BS 970 (Part 1) 590H17?
IS 11169 (Part 1) 20Mn5Cr5S3 and BS 970 (Part 1) 590H17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.