Close Alternative — 78.1% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 20Mo5Cr2 (IS 11169 (Part 1):2022) and SAE J404 4118 (SAE J404:2009) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 20Mo5Cr2 is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while SAE J404 4118 is commonly used for gears, camshafts, pins and lightly stressed automotive components.
IS 11169 (Part 1) 20Mo5Cr2 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 4118 is defined under SAE International, originating from United States.
As per chemical composition, IS 11169 (Part 1) 20Mo5Cr2 vs SAE J404 4118 is a 78.1% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 78.1%.
Frequently Compared With IS 11169 (Part 1) 20Mo5Cr2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 20Mo5Cr2
SAE J404 4118
Hardness, ferrite-pearlite (+FP)
140-187 HB
Not specified
Tensile Strength, annealed (+AC)
<=560 MPa (over 5 to 40 mm)
Not specified
Typical Applications
IS 11169 (Part 1) 20Mo5Cr2
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
SAE J404 4118
Gears, camshafts, pins and lightly stressed automotive components
Key Differences
IS 11169 (Part 1) 20Mo5Cr2 specifies Cu which is not specified for SAE J404 4118.
Can IS 11169 (Part 1) 20Mo5Cr2 Be Substituted With SAE J404 4118?
IS 11169 (Part 1) 20Mo5Cr2 and SAE J404 4118 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 11169 (Part 1) 20Mo5Cr2 and SAE J404 4118?
IS 11169 (Part 1) 20Mo5Cr2 specifies Cu which is not specified for SAE J404 4118.
Can IS 11169 (Part 1) 20Mo5Cr2 be substituted with SAE J404 4118?
IS 11169 (Part 1) 20Mo5Cr2 and SAE J404 4118 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.