IS 11169 (Part 1) 20Ni6Cr3Mo3S3 vs BS 970 (Part 1) 817M40

Related Material — 65.4% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 20Ni6Cr3Mo3S3 (IS 11169 (Part 1):2022) and BS 970 (Part 1) 817M40 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 20Ni6Cr3Mo3S3 is typically used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b), while BS 970 (Part 1) 817M40 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. IS 11169 (Part 1) 20Ni6Cr3Mo3S3 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 817M40 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 20Ni6Cr3Mo3S3 vs BS 970 (Part 1) 817M40 is a 65.4% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 65.4%.

Frequently Compared With IS 11169 (Part 1) 20Ni6Cr3Mo3S3:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H
Match Breakdown
CHEMISTRY MATCH
65.4%
MECHANICAL MATCH
No shared data
OVERALL
65.4%
Specifications
Property IS 11169 (Part 1) 20Ni6Cr3Mo3S3 BS 970 (Part 1) 817M40
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.16-0.23 0.36-0.44
Cr (%) 0.60-0.90 1.00-1.40
Cu (%) <=0.25 Not specified
Mn (%) 0.50-0.90 0.45-0.70
Mo (%) 0.25-0.35 0.20-0.35
Ni (%) 1.40-1.70 1.30-1.70
P (%) <=0.025 <=0.035
S (%) 0.020-0.040 <=0.040
Si (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 20Ni6Cr3Mo3S3 BS 970 (Part 1) 817M40
Hardness, ferrite-pearlite (+FP) 149-201 HB Not specified
Tensile Strength, annealed (+AC) <=610 MPa (over 5 to 25 mm) Not specified
Typical Applications
IS 11169 (Part 1) 20Ni6Cr3Mo3S3
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
BS 970 (Part 1) 817M40
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
Can IS 11169 (Part 1) 20Ni6Cr3Mo3S3 Be Substituted With BS 970 (Part 1) 817M40?
IS 11169 (Part 1) 20Ni6Cr3Mo3S3 and BS 970 (Part 1) 817M40 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 20Ni6Cr3Mo3S3
0 active listings and RFQs →
BS 970 (Part 1) 817M40
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 20Ni6Cr3Mo3S3 and BS 970 (Part 1) 817M40?
IS 11169 (Part 1) 20Ni6Cr3Mo3S3 specifies Cu, Si which are not specified for BS 970 (Part 1) 817M40.
Can IS 11169 (Part 1) 20Ni6Cr3Mo3S3 be substituted with BS 970 (Part 1) 817M40?
IS 11169 (Part 1) 20Ni6Cr3Mo3S3 and BS 970 (Part 1) 817M40 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.