IS 11169 (Part 1):2022 22C10BT Steel: Specifications & Listings
IS 11169 (Part 1):2022 22C10BT: Cold heading quality boron alloyed case hardening steel 22C10BT to IS 11169 (Part 1):2022, for parts case hardened after cold heading or cold extrusion, supplied as wire rod, bars or wire of 2 to 100 mm. Maximum tensile strength as hot rolled is 600 MPa. It can be ordered with hardenability requirements (H).
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
B
C
Cu
Mn
P
S
Si
0.0008-0.005
0.20-0.24
<=0.25
0.90-1.20
<=0.025
<=0.025
<=0.30
Mechanical Properties
Tensile Strength, as rolled (+AR)
<=600 MPa (over 5 to 40 mm)
More data from IS 11169 (Part 1):2022
From the standard
Other composition limitsfrom the table notes and clauses
Values
Maximum unless a range is given (ladle analysis)
Ordered with hardenability
Small deviations from these limits are allowed (not for sulphur and phosphorus): up to 0.01 percent for carbon and the Table 1 values for other elements
Deoxidation
Aluminium killed (clause 6.2)
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 1):2022, Table B.2 and its notes, clause 6.2
Tensile strength and reduction of area by delivery conditionby delivery condition and size
Delivery condition
Diameter (mm)
Tensile strength, max (MPa)
Reduction of area, min (%)
+AR
over 5 to 10
600
55
+AR
over 10 to 40
600
55
+AC or +AC+PE
over 5 to 10
520
62
+AC or +AC+PE
over 10 to 40
520
62
+AR+C
over 5 to 10
720
53
+AR+C
over 10 to 40
710
53
+AR+C+AC
2 (incl.) to 5
520
64
+AR+C+AC
over 5 to 10
500
64
+AR+C+AC
over 10 to 40
500
64
+AR+C+AC+LC
2 (incl.) to 5
560
62
+AR+C+AC+LC
over 5 to 10
540
62
+AR+C+AC+LC
over 10 to 40
540
62
+AC+C
over 5 to 10
630
59
+AC+C
over 10 to 40
620
59
Codes: +AR as hot rolled, +PE peeled, +C cold drawn, +AC annealed to spheroidized carbides, +LC skin passed. For non-circular sections the properties are agreed between manufacturer and purchaser. Reduction of area values in the as rolled condition are for information only.
Source: IS 11169 (Part 1):2022, Table B.4
Hardenability, end quench test (H)Hardness band
Hardness band (HRC, minimum to maximum) by distance from the quenched end (mm)
1.5
3
5
7
9
11
13
15
20
25
30
35
40
Distance from quenched end (mm)
1.5
3
5
7
9
11
13
15
20
25
30
35
40
Maximum, HRC
49
48
47
45
42
39
35
32
24
20
-
-
-
Minimum, HRC
43
41
40
32
23
-
-
-
-
-
-
-
-
Applies when ordered with the symbol H; otherwise for guidance only. Jominy test as per IS 3848, austenitizing at 880 ± 5 °C.
Source: IS 11169 (Part 1):2022, Table B.6