IS 11169 (Part 1) 25C9GC vs BS 970 (Part 3) 070M55

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 25C9GC (IS 11169 (Part 1):2022) and BS 970 (Part 3) 070M55 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. IS 11169 (Part 1) 25C9GC is typically used for cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex a), while BS 970 (Part 3) 070M55 is commonly used for used for springs, blades, wear plates, hand tools, shafts, and cutting components.. IS 11169 (Part 1) 25C9GC is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 070M55 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 25C9GC vs BS 970 (Part 3) 070M55 is a 57.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 1) 25C9GC:
BS 970 (Part 1) 080A20 BS 970 (Part 1) 040A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
57.2%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 11169 (Part 1) 25C9GC BS 970 (Part 3) 070M55
Standard IS 11169 (Part 1):2022 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
Al (%) <=0.015 Not specified
C (%) 0.23-0.27 0.50-0.60
Cr (%) <=0.30 Not specified
Cu (%) <=0.30 Not specified
Mn (%) 0.80-1.00 0.50-0.90
Mo (%) <=0.10 Not specified
Ni (%) <=0.30 Not specified
P (%) <=0.025 <=0.05
S (%) <=0.025 <=0.05
Si (%) 0.15-0.25 0.10-0.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 25C9GC BS 970 (Part 3) 070M55
Reduction of Area, as rolled (+AR) >=50% (for information) Not specified
Tensile Strength, as rolled (+AR) <=590 MPa (over 5 to 100 mm) Not specified
Typical Applications
IS 11169 (Part 1) 25C9GC
Cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex A)
BS 970 (Part 3) 070M55
Used for springs, blades, wear plates, hand tools, shafts, and cutting components.
Key Differences
Can IS 11169 (Part 1) 25C9GC Be Substituted With BS 970 (Part 3) 070M55?
IS 11169 (Part 1) 25C9GC and BS 970 (Part 3) 070M55 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 11169 (Part 1) 25C9GC
No active listings currently.
BS 970 (Part 3) 070M55
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–5800 mm (188.98–228.35 in)
On M-EX Right Now
IS 11169 (Part 1) 25C9GC
0 active listings and RFQs →
BS 970 (Part 3) 070M55
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 25C9GC and BS 970 (Part 3) 070M55?
IS 11169 (Part 1) 25C9GC specifies Al, Cr, Cu, Mo which are not specified for BS 970 (Part 3) 070M55.
Can IS 11169 (Part 1) 25C9GC be substituted with BS 970 (Part 3) 070M55?
IS 11169 (Part 1) 25C9GC and BS 970 (Part 3) 070M55 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.