IS 11169 (Part 1) 2C3 vs EN 10088-1 X2CrAlSiNb18

Related Material — 64.7% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 2C3 (IS 11169 (Part 1):2022) and EN 10088-1 X2CrAlSiNb18 (EN 10088-1:2023) are both steel grades. IS 11169 (Part 1) 2C3 is classified under Carbon Steel, while EN 10088-1 X2CrAlSiNb18 is classified under Stainless Steel — a different category, which is worth noting alongside the chemistry match below. IS 11169 (Part 1) 2C3 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrAlSiNb18 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 1) 2C3 vs EN 10088-1 X2CrAlSiNb18 is a 64.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 64.7%.

Frequently Compared With IS 11169 (Part 1) 2C3:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 3) 045A10
Match Breakdown
CHEMISTRY MATCH
64.7%
MECHANICAL MATCH
No shared data
OVERALL
64.7%
Specifications
Property IS 11169 (Part 1) 2C3 EN 10088-1 X2CrAlSiNb18
Standard IS 11169 (Part 1):2022 EN 10088-1:2023
Category Carbon Steel Stainless Steel
Al (%) 0.020-0.060 0.20-1.50
C (%) <=0.03 <=0.030
Cr (%) <=0.30 17.5-18.5
Cu (%) <=0.30 <=0.50
Mn (%) 0.20-0.40 <=1.00
Mo (%) <=0.10 <=0.50
Ni (%) <=0.30 <=0.50
P (%) <=0.020 <=0.050
S (%) <=0.025 <=0.050
Si (%) <=0.10 0.20-1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 2C3 EN 10088-1 X2CrAlSiNb18
Reduction of Area, as rolled (+AR) >=75% (for information) Not specified
Tensile Strength, as rolled (+AR) <=360 MPa (over 5 to 100 mm) Not specified
Typical Applications
IS 11169 (Part 1) 2C3
Cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex A)
EN 10088-1 X2CrAlSiNb18
Not documented
Key Differences
Can IS 11169 (Part 1) 2C3 Be Substituted With EN 10088-1 X2CrAlSiNb18?
IS 11169 (Part 1) 2C3 and EN 10088-1 X2CrAlSiNb18 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 2C3
0 active listings and RFQs →
EN 10088-1 X2CrAlSiNb18
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 2C3 and EN 10088-1 X2CrAlSiNb18?
Different category: IS 11169 (Part 1) 2C3 is Carbon Steel, EN 10088-1 X2CrAlSiNb18 is Stainless Steel.
Can IS 11169 (Part 1) 2C3 be substituted with EN 10088-1 X2CrAlSiNb18?
IS 11169 (Part 1) 2C3 and EN 10088-1 X2CrAlSiNb18 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.