IS 11169 (Part 1):2022 30Ni13Cr5 Steel: Specifications & Listings

IS 11169 (Part 1):2022 30Ni13Cr5: Cold heading quality alloy steel 30Ni13Cr5 to IS 11169 (Part 1):2022 for quenching and tempering after cold heading or cold extrusion, supplied as wire rod, bars or wire of 2 to 100 mm. Maximum hardness in the annealed condition is 200 HBW.

Category: Alloy Steel
Grade Details
GradeIS 11169 (Part 1):2022 30Ni13Cr5
Standard IS 11169 (Part 1):2022
ApplicationsCold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 11169 (Part 1) 30Ni13Cr5 IS 11169 (Part 1):1984 India 2 listings, 0 RFQs →
IS 5517 30Ni13Cr5 IS 5517:1993 India No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
IS 11169 (Part 1) 30Ni13Cr5 IS 11169 (Part 1):1984 Strong Match
IS 11169 (Part 1) 15Ni16Cr5 IS 11169 (Part 1):1984 Close Alternative
IS 11169 (Part 1) 15Ni5Cr5 IS 11169 (Part 1):2022 Close Alternative
BS 970 EN39A BS 970:1955 Close Alternative
IS 1570 (Part 4) 13Ni13Cr3 IS 1570 (Part 4):1988 Related Material
IS 1570 (Part 4) 15Cr6Ni6 IS 1570 (Part 4):1988 Related Material
BS 970 EN36B BS 970:1955 Related Material
BS 970 (Part 3) 655M13 BS 970 (Part 3):1991 Related Material
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Cr Cu Mn Mo Ni P S Si
0.26-0.34 1.10-1.45 <=0.15 0.40-0.70 <=0.05 3.90-4.30 <=0.035 <=0.035 0.10-0.35
Mechanical Properties
Hardness, annealed (+AC) <=200 HBW

More data from IS 11169 (Part 1):2022

From the standard
Other composition limits from the table notes and clauses
Values
Maximum unless a range is given (ladle analysis)
Residual elements, maximum
Sn 0.020, V 0.05 percent; Cr + Ni + Cu + Sn + Mo + V together not over 0.40 percent, where not used as alloying elements
Deoxidation
Aluminium killed (clause 6.2)
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 1):2022, Table C.2 and its notes, clause 6.2
Hardness in the annealed condition 1 condition
Annealed (+AC), maximum
200 HBW
Brinell hardness for products delivered in the annealed condition. Printed as 30Ni3Cr5 in Table C.6.
Source: IS 11169 (Part 1):2022, Table C.6, clause 8.1

Active IS 11169 (Part 1):2022 30Ni13Cr5 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 1):2022 30Ni13Cr5 listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 1):2022 30Ni13Cr5

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 1):2022 30Ni13Cr5 at this time.

Register for Alerts