IS 11169 (Part 1) 34C14BT vs IS 11169 (Part 1) 35C14BT

Strong Match — 85.7% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 34C14BT (IS 11169 (Part 1):2022) and IS 11169 (Part 1) 35C14BT (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 34C14BT is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while IS 11169 (Part 1) 35C14BT is commonly used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c). IS 11169 (Part 1) 34C14BT is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 35C14BT is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 34C14BT vs IS 11169 (Part 1) 35C14BT is a 85.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85.7%.

Frequently Compared With IS 11169 (Part 1) 34C14BT:
NF A35-565 100C6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Mo6 UNI 11234 100Cr6
Match Breakdown
CHEMISTRY MATCH
85.7%
MECHANICAL MATCH
No shared data
OVERALL
85.7%
Specifications
Property IS 11169 (Part 1) 34C14BT IS 11169 (Part 1) 35C14BT
Standard IS 11169 (Part 1):2022 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
B (%) 0.0005-0.003 0.0008-0.005
C (%) 0.32-0.37 0.31-0.37
Cr (%) <=0.15 <=0.30
Cu (%) <=0.15 <=0.25
Mn (%) 1.20-1.50 1.20-1.50
Mo (%) <=0.05 Not specified
P (%) <=0.035 <=0.025
S (%) <=0.035 <=0.025
Si (%) 0.15-0.30 <=0.30
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 34C14BT IS 11169 (Part 1) 35C14BT
Core Hardness (CH) >=40 HRC up to 26 mm Not specified
Hardness, annealed (+AC) <=190 HBW Not specified
Tensile Strength, cold drawn, annealed and skin passed (+AR+C+AC+LC) Not specified <=680 MPa (over 5 to 40 mm)
Typical Applications
IS 11169 (Part 1) 34C14BT
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
IS 11169 (Part 1) 35C14BT
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Key Differences
Can IS 11169 (Part 1) 34C14BT Be Substituted With IS 11169 (Part 1) 35C14BT?
IS 11169 (Part 1) 34C14BT and IS 11169 (Part 1) 35C14BT overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 35C14BT is often considered as a substitute for IS 11169 (Part 1) 34C14BT in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 1) 34C14BT
0 active listings and RFQs →
IS 11169 (Part 1) 35C14BT
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 34C14BT and IS 11169 (Part 1) 35C14BT?
IS 11169 (Part 1) 34C14BT specifies Mo which is not specified for IS 11169 (Part 1) 35C14BT.
Can IS 11169 (Part 1) 34C14BT be substituted with IS 11169 (Part 1) 35C14BT?
IS 11169 (Part 1) 34C14BT and IS 11169 (Part 1) 35C14BT overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 35C14BT is often considered as a substitute for IS 11169 (Part 1) 34C14BT in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.