Post Stock Login Register

IS 11169 (Part 1) 35C7S3 vs SAE J403 1037

Close Alternative — 84.7% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 35C7S3 (IS 11169 (Part 1):2022) and SAE J403 1037 (SAE J403:2009) are both steel grades. Both fall under the Carbon Steel category. IS 11169 (Part 1) 35C7S3 is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while SAE J403 1037 is commonly used for chemistry-only grade; product scope as listed in the composition notes. IS 11169 (Part 1) 35C7S3 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J403 1037 is defined under SAE International, originating from United States.

As per chemical composition, IS 11169 (Part 1) 35C7S3 vs SAE J403 1037 is a 84.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.7%.

Frequently Compared With IS 11169 (Part 1) 35C7S3:
BS 970 (Part 1) 040A10 BS 970 (Part 3) 070M55 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 060A32
Match Breakdown
CHEMISTRY MATCH
84.7%
MECHANICAL MATCH
No shared data
OVERALL
84.7%
Specifications
Property IS 11169 (Part 1) 35C7S3 SAE J403 1037
Standard IS 11169 (Part 1):2022 SAE J403:2009
Category Carbon Steel Carbon Steel
C (%) 0.32-0.39 0.32-0.38
Cu (%) <=0.25 Not specified
Mn (%) 0.50-0.80 0.70-1.00
P (%) <=0.025 <=0.030
S (%) 0.020-0.035 <=0.050
Si (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 35C7S3 SAE J403 1037
Tensile Strength, annealed (+AC) <=560 MPa (over 5 to 40 mm) Not specified
Typical Applications
IS 11169 (Part 1) 35C7S3
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
SAE J403 1037
Chemistry-only grade; product scope as listed in the composition notes
Key Differences
Can IS 11169 (Part 1) 35C7S3 Be Substituted With SAE J403 1037?
IS 11169 (Part 1) 35C7S3 and SAE J403 1037 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 1) 35C7S3
0 active listings and RFQs →
SAE J403 1037
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 35C7S3 and SAE J403 1037?
IS 11169 (Part 1) 35C7S3 specifies Cu, Si which are not specified for SAE J403 1037.
Can IS 11169 (Part 1) 35C7S3 be substituted with SAE J403 1037?
IS 11169 (Part 1) 35C7S3 and SAE J403 1037 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.