IS 11169 (Part 1) 35C8BT vs IS 4367 07Cr4Mo6

Minimal Match — 53.5% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 35C8BT (IS 11169 (Part 1):2022) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 35C8BT is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 1) 35C8BT vs IS 4367 07Cr4Mo6 is a 53.5% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 53.5%.

Frequently Compared With IS 11169 (Part 1) 35C8BT:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr4 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 07Cr4Mo6
Match Breakdown
CHEMISTRY MATCH
53.5%
MECHANICAL MATCH
No shared data
OVERALL
53.5%
Specifications
Property IS 11169 (Part 1) 35C8BT IS 4367 07Cr4Mo6
Standard IS 11169 (Part 1):2022 IS 4367:1991
Category Alloy Steel Alloy Steel
B (%) 0.0005-0.003 Not specified
C (%) 0.32-0.38 <=0.12
Cr (%) <=0.20 0.70-1.10
Cu (%) <=0.35 Not specified
Mn (%) 0.60-0.90 0.40-0.70
Mo (%) <=0.060 0.45-0.65
Ni (%) <=0.25 <=0.30
P (%) <=0.040 <=0.035
S (%) <=0.050 <=0.035
Si (%) Not specified 0.15-0.60
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 35C8BT IS 4367 07Cr4Mo6
Tensile Strength Not specified 380-550 MPa
Yield Strength Not specified 225 MPa min
Elongation Not specified >=19%
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Condition Not specified Normalised and tempered, ruling section up to 40 mm
Typical Applications
IS 11169 (Part 1) 35C8BT
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
IS 4367 07Cr4Mo6
Not documented
Key Differences
Can IS 11169 (Part 1) 35C8BT Be Substituted With IS 4367 07Cr4Mo6?
IS 11169 (Part 1) 35C8BT and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 35C8BT
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 35C8BT and IS 4367 07Cr4Mo6?
IS 11169 (Part 1) 35C8BT specifies B, Cu which are not specified for IS 4367 07Cr4Mo6. IS 4367 07Cr4Mo6 specifies Si which is not specified for IS 11169 (Part 1) 35C8BT.
Can IS 11169 (Part 1) 35C8BT be substituted with IS 4367 07Cr4Mo6?
IS 11169 (Part 1) 35C8BT and IS 4367 07Cr4Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.