IS 11169 (Part 1) 37C13BT vs IS 11169 (Part 1) 38C8BT
Close Alternative — 79.5% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 37C13BT (IS 11169 (Part 1):2022) and IS 11169 (Part 1) 38C8BT (IS 11169 (Part 1):2022) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 37C13BT is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while IS 11169 (Part 1) 38C8BT is commonly used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c).
IS 11169 (Part 1) 37C13BT is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 38C8BT is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 1) 37C13BT vs IS 11169 (Part 1) 38C8BT is a 94.3% match.
As per mechanical properties, the match is 50%.
Combined, this makes them a close alternative overall at 79.5%.
Frequently Compared With IS 11169 (Part 1) 37C13BT:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 37C13BT
IS 11169 (Part 1) 38C8BT
Core Hardness (CH)
>=48 HRC up to 16 mm
>=48 HRC up to 11 mm
Tensile Strength, annealed (+AC)
<=620 MPa (over 5 to 40 mm)
<=570 MPa (over 5 to 40 mm)
Typical Applications
IS 11169 (Part 1) 37C13BT
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
IS 11169 (Part 1) 38C8BT
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Can IS 11169 (Part 1) 37C13BT Be Substituted With IS 11169 (Part 1) 38C8BT?
IS 11169 (Part 1) 37C13BT and IS 11169 (Part 1) 38C8BT are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 11169 (Part 1) 37C13BT and IS 11169 (Part 1) 38C8BT?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 1) 37C13BT be substituted with IS 11169 (Part 1) 38C8BT?
IS 11169 (Part 1) 37C13BT and IS 11169 (Part 1) 38C8BT are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.