IS 11169 (Part 1) 37Cr4Mo2 vs BS 970 (Part 1) 708A37

Strong Match — 86.3% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 37Cr4Mo2 (IS 11169 (Part 1):2022) and BS 970 (Part 1) 708A37 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 37Cr4Mo2 is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while BS 970 (Part 1) 708A37 is commonly used for used for gears, shafts, studs, machine spindles, crankshafts, and automotive components.. IS 11169 (Part 1) 37Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 708A37 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 37Cr4Mo2 vs BS 970 (Part 1) 708A37 is a 86.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.3%.

Frequently Compared With IS 11169 (Part 1) 37Cr4Mo2:
IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
86.3%
MECHANICAL MATCH
No shared data
OVERALL
86.3%
Specifications
Property IS 11169 (Part 1) 37Cr4Mo2 BS 970 (Part 1) 708A37
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1983
Category Alloy Steel Alloy Steel
C (%) 0.35-0.40 0.35-0.40
Cr (%) 0.90-1.20 0.90-1.20
Cu (%) <=0.25 Not specified
Mn (%) 0.60-0.90 0.70-0.90
Mo (%) 0.15-0.30 0.15-0.25
P (%) <=0.025 <=0.035
S (%) <=0.025 <=0.040
Si (%) <=0.30 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 37Cr4Mo2 BS 970 (Part 1) 708A37
Core Hardness (CH) >=48 HRC up to 18 mm Not specified
Tensile Strength, annealed (+AC) <=620 MPa (over 5 to 40 mm) Not specified
Typical Applications
IS 11169 (Part 1) 37Cr4Mo2
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
BS 970 (Part 1) 708A37
Used for gears, shafts, studs, machine spindles, crankshafts, and automotive components.
Key Differences
Can IS 11169 (Part 1) 37Cr4Mo2 Be Substituted With BS 970 (Part 1) 708A37?
IS 11169 (Part 1) 37Cr4Mo2 and BS 970 (Part 1) 708A37 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 708A37 is often considered as a substitute for IS 11169 (Part 1) 37Cr4Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 11169 (Part 1) 37Cr4Mo2
No active listings currently.
BS 970 (Part 1) 708A37
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 6700–7000 mm (263.78–275.59 in)
On M-EX Right Now
IS 11169 (Part 1) 37Cr4Mo2
0 active listings and RFQs →
BS 970 (Part 1) 708A37
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 37Cr4Mo2 and BS 970 (Part 1) 708A37?
IS 11169 (Part 1) 37Cr4Mo2 specifies Cu, Si which are not specified for BS 970 (Part 1) 708A37.
Can IS 11169 (Part 1) 37Cr4Mo2 be substituted with BS 970 (Part 1) 708A37?
IS 11169 (Part 1) 37Cr4Mo2 and BS 970 (Part 1) 708A37 overlap closely enough on chemistry and mechanical properties that BS 970 (Part 1) 708A37 is often considered as a substitute for IS 11169 (Part 1) 37Cr4Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.