IS 11169 (Part 1):2022 37Mo2 Steel: Specifications & Listings
IS 11169 (Part 1):2022 37Mo2: Cold heading quality alloy steel 37Mo2 to IS 11169 (Part 1):2022 for quenching and tempering after cold heading or cold extrusion, supplied as wire rod, bars or wire of 2 to 100 mm. Maximum tensile strength annealed is 570 MPa. It can be ordered with hardenability requirements (H, HH or HL, CH).
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Cu
Mn
Mo
P
S
Si
0.35-0.40
<=0.25
0.60-0.90
0.20-0.30
<=0.025
<=0.025
<=0.30
Mechanical Properties
Core Hardness (CH)
>=48 HRC up to 8 mm
Tensile Strength, annealed (+AC)
<=570 MPa (over 5 to 40 mm)
More data from IS 11169 (Part 1):2022
From the standard
Other composition limitsfrom the table notes and clauses
Values
Maximum unless a range is given (ladle analysis)
Silicon
Lower silicon contents may be agreed when ordering, with due regard to the effect on properties such as hardenability
Ordered with hardenability
Small deviations from these limits are allowed (not for sulphur and phosphorus): up to 0.01 percent for carbon and the Table 1 values for other elements
Deoxidation
Aluminium killed (clause 6.2)
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 1):2022, Table C.2 and its notes, clause 6.2
Tensile strength and reduction of area by delivery conditionby delivery condition and size
Delivery condition
Diameter (mm)
Tensile strength, max (MPa)
Reduction of area, min (%)
+AC or +AC+PE
over 5 to 40
570
59
+AC+C+AC
2 (incl.) to 5
560
61
+AC+C+AC
over 5 to 40
550
61
+AC+C+AC+LC
2 (incl.) to 5
600
59
+AC+C+AC+LC
over 5 to 40
590
59
Codes: +AR as hot rolled, +PE peeled, +C cold drawn, +AC annealed to spheroidized carbides, +LC skin passed. For non-circular sections the properties are agreed between manufacturer and purchaser.
Source: IS 11169 (Part 1):2022, Table C.5
Hardenability, end quench test (H)Hardness band
Hardness band (HRC, minimum to maximum) by distance from the quenched end (mm)
1.5
3
5
7
9
11
13
15
20
25
30
35
40
45
50
Distance from quenched end (mm)
1.5
3
5
7
9
11
13
15
20
25
30
35
40
45
50
Maximum, HRC
59
57
53
47
41
36
32
29
27
25
-
-
-
-
-
Minimum, HRC
51
48
41
33
27
26
22
20
-
-
-
-
-
-
-
Applies when ordered with the symbol H; otherwise for guidance only. Jominy test as per IS 3848, austenitizing at 850 ± 5 °C.
Source: IS 11169 (Part 1):2022, Table C.9
Restricted hardenability bands, HH and HL (HRC by distance from quenched end, mm)HH and HL ordering
Band
1.5
3
5
7
9
11
13
15
20
25
30
35
40
45
50
HH maximum
59
57
53
47
41
36
32
29
27
25
-
-
-
-
-
HH minimum
54
51
45
38
32
29
25
23
-
-
-
-
-
-
-
HL maximum
56
54
49
42
36
33
29
26
-
-
-
-
-
-
-
HL minimum
51
48
41
33
27
26
22
20
-
-
-
-
-
-
-
HH: the upper limit matches the H band upper limit; HL: the lower limit matches the H band lower limit. Austenitizing at 850 ± 5 °C. Not applicable to steels ordered with a restricted range of carbon content.
Source: IS 11169 (Part 1):2022, Table C.11
Core hardening (CH)CH ordering
Austenitizing temperature
850 °C ± 5
Minimum core hardness, 90 percent martensite
48 HRC
Maximum diameter for 90 percent martensite in the core
8 mm
Applies when ordered with the symbol CH. The diameter is the one reached with the lowest hardenability of the grade; HH grades allow a larger diameter. A hardening time of at least 30 minutes at temperature is recommended.
Source: IS 11169 (Part 1):2022, Table C.12, clauses 8.2.4 and 8.2.6