IS 11169 (Part 1) 41Cr2Ni2Mo2 vs SAE J404 8637

Strong Match — 86.6% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 41Cr2Ni2Mo2 (IS 11169 (Part 1):2022) and SAE J404 8637 (SAE J404:2000) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 41Cr2Ni2Mo2 is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while SAE J404 8637 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. IS 11169 (Part 1) 41Cr2Ni2Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 8637 is defined under SAE International, originating from United States.

As per chemical composition, IS 11169 (Part 1) 41Cr2Ni2Mo2 vs SAE J404 8637 is a 86.6% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 86.6%.

Frequently Compared With IS 11169 (Part 1) 41Cr2Ni2Mo2:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 11169 (Part 1) 10Ni5Cr4 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 1570 (Part 7) 10Mo6H IS 4367 07Cr4Mo6 UNI 11234 100Cr6
Match Breakdown
CHEMISTRY MATCH
86.6%
MECHANICAL MATCH
No shared data
OVERALL
86.6%
Specifications
Property IS 11169 (Part 1) 41Cr2Ni2Mo2 SAE J404 8637
Standard IS 11169 (Part 1):2022 SAE J404:2000
Category Alloy Steel Alloy Steel
C (%) 0.37-0.44 0.38-0.43
Cr (%) 0.40-0.60 0.40-0.60
Cu (%) <=0.25 Not specified
Mn (%) 0.70-1.00 0.75-1.00
Mo (%) 0.15-0.30 0.15-0.25
Ni (%) 0.40-0.70 0.40-0.70
P (%) <=0.025 <=0.030
S (%) <=0.025 <=0.040
Si (%) <=0.30 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 41Cr2Ni2Mo2 SAE J404 8637
Tensile Strength, annealed, cold drawn and annealed (+AC+C+AC) <=640 MPa (over 5 to 40 mm) Not specified
Typical Applications
IS 11169 (Part 1) 41Cr2Ni2Mo2
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
SAE J404 8637
Chemistry-only alloy steel grade; see the composition notes for product scope
Key Differences
Can IS 11169 (Part 1) 41Cr2Ni2Mo2 Be Substituted With SAE J404 8637?
IS 11169 (Part 1) 41Cr2Ni2Mo2 and SAE J404 8637 overlap closely enough on chemistry and mechanical properties that SAE J404 8637 is often considered as a substitute for IS 11169 (Part 1) 41Cr2Ni2Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 1) 41Cr2Ni2Mo2
0 active listings and RFQs →
SAE J404 8637
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 41Cr2Ni2Mo2 and SAE J404 8637?
IS 11169 (Part 1) 41Cr2Ni2Mo2 specifies Cu which is not specified for SAE J404 8637.
Can IS 11169 (Part 1) 41Cr2Ni2Mo2 be substituted with SAE J404 8637?
IS 11169 (Part 1) 41Cr2Ni2Mo2 and SAE J404 8637 overlap closely enough on chemistry and mechanical properties that SAE J404 8637 is often considered as a substitute for IS 11169 (Part 1) 41Cr2Ni2Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.