Close Alternative — 79.6% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 41Cr4S3 (IS 11169 (Part 1):2022) and SAE J404 5140 (SAE J404:2009) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 41Cr4S3 is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while SAE J404 5140 is commonly used for used for gears, shafts, spindles, automotive parts, bolts, and machine components..
IS 11169 (Part 1) 41Cr4S3 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 5140 is defined under SAE International, originating from United States.
As per chemical composition, IS 11169 (Part 1) 41Cr4S3 vs SAE J404 5140 is a 79.6% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 79.6%.
Frequently Compared With IS 11169 (Part 1) 41Cr4S3:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 41Cr4S3
SAE J404 5140
Core Hardness (CH)
>=50 HRC up to 16 mm
Not specified
Tensile Strength, annealed (+AC)
<=620 MPa (over 5 to 40 mm)
Not specified
Typical Applications
IS 11169 (Part 1) 41Cr4S3
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
SAE J404 5140
Used for gears, shafts, spindles, automotive parts, bolts, and machine components.
Key Differences
IS 11169 (Part 1) 41Cr4S3 specifies Cu which is not specified for SAE J404 5140.
Can IS 11169 (Part 1) 41Cr4S3 Be Substituted With SAE J404 5140?
IS 11169 (Part 1) 41Cr4S3 and SAE J404 5140 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 11169 (Part 1) 41Cr4S3 and SAE J404 5140?
IS 11169 (Part 1) 41Cr4S3 specifies Cu which is not specified for SAE J404 5140.
Can IS 11169 (Part 1) 41Cr4S3 be substituted with SAE J404 5140?
IS 11169 (Part 1) 41Cr4S3 and SAE J404 5140 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.