IS 11169 (Part 1) 41Ni7Cr3Mo2 (IS 11169 (Part 1):2022) and SAE J404 8640 (SAE J404:2009) are both steel grades. Both fall under the Alloy Steel category. IS 11169 (Part 1) 41Ni7Cr3Mo2 is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while SAE J404 8640 is commonly used for chemistry-only alloy steel grade; see the composition notes for product scope. IS 11169 (Part 1) 41Ni7Cr3Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J404 8640 is defined under SAE International, originating from United States.

As per chemical composition, IS 11169 (Part 1) 41Ni7Cr3Mo2 vs SAE J404 8640 is a 67.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 67.9%.

Frequently Compared With IS 11169 (Part 1) 41Ni7Cr3Mo2:
IS 1570 (Part 4) 103Cr4 NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Mo6H IS 11169 (Part 1) 10Ni5Cr4 IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 105Cr5 IS 4367 10Cr9Mo10 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6
Match Breakdown
CHEMISTRY MATCH
67.9%
MECHANICAL MATCH
No shared data
OVERALL
67.9%
Specifications
Property IS 11169 (Part 1) 41Ni7Cr3Mo2 SAE J404 8640
Standard IS 11169 (Part 1):2022 SAE J404:2009
Category Alloy Steel Alloy Steel
C (%) 0.38-0.44 0.38-0.43
Cr (%) 0.70-0.90 0.40-0.60
Cu (%) <=0.25 Not specified
Mn (%) 0.60-0.90 0.75-1.00
Mo (%) 0.15-0.30 0.15-0.25
Ni (%) 1.65-2.00 0.40-0.70
P (%) <=0.025 <=0.030
S (%) <=0.025 <=0.040
Si (%) <=0.30 0.15-0.35
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 41Ni7Cr3Mo2 SAE J404 8640
Core Hardness (CH) >=50 HRC up to 34 mm Not specified
Tensile Strength, annealed (+AC) <=720 MPa (over 5 to 40 mm) Not specified
Typical Applications
IS 11169 (Part 1) 41Ni7Cr3Mo2
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
SAE J404 8640
Chemistry-only alloy steel grade; see the composition notes for product scope
Key Differences
Can IS 11169 (Part 1) 41Ni7Cr3Mo2 Be Substituted With SAE J404 8640?
IS 11169 (Part 1) 41Ni7Cr3Mo2 and SAE J404 8640 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 41Ni7Cr3Mo2
0 active listings and RFQs →
SAE J404 8640
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 41Ni7Cr3Mo2 and SAE J404 8640?
IS 11169 (Part 1) 41Ni7Cr3Mo2 specifies Cu which is not specified for SAE J404 8640.
Can IS 11169 (Part 1) 41Ni7Cr3Mo2 be substituted with SAE J404 8640?
IS 11169 (Part 1) 41Ni7Cr3Mo2 and SAE J404 8640 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.