IS 11169 (Part 1) 42Cr4Mo2 vs BS 970 (Part 1) 708M40
Close Alternative — 81.5% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 42Cr4Mo2 (IS 11169 (Part 1):2022) and BS 970 (Part 1) 708M40 (BS 970 (Part 1):1991) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 42Cr4Mo2 is typically used for cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex c), while BS 970 (Part 1) 708M40 is commonly used for used for axles, gears, shafts, studs, crankshafts, and heavy-duty machinery parts..
IS 11169 (Part 1) 42Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 708M40 is defined under British Standards (BS), originating from United Kingdom.
As per chemical composition, IS 11169 (Part 1) 42Cr4Mo2 vs BS 970 (Part 1) 708M40 is a 81.5% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 81.5%.
Frequently Compared With IS 11169 (Part 1) 42Cr4Mo2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 42Cr4Mo2
BS 970 (Part 1) 708M40
Core Hardness (CH)
>=50 HRC up to 21 mm
Not specified
Tensile Strength, annealed (+AC)
<=630 MPa (over 5 to 40 mm)
Not specified
Typical Applications
IS 11169 (Part 1) 42Cr4Mo2
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
BS 970 (Part 1) 708M40
Used for axles, gears, shafts, studs, crankshafts, and heavy-duty machinery parts.
Key Differences
IS 11169 (Part 1) 42Cr4Mo2 specifies Cu, P, S, Si which are not specified for BS 970 (Part 1) 708M40.
Can IS 11169 (Part 1) 42Cr4Mo2 Be Substituted With BS 970 (Part 1) 708M40?
IS 11169 (Part 1) 42Cr4Mo2 and BS 970 (Part 1) 708M40 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 11169 (Part 1) 42Cr4Mo2 and BS 970 (Part 1) 708M40?
IS 11169 (Part 1) 42Cr4Mo2 specifies Cu, P, S, Si which are not specified for BS 970 (Part 1) 708M40.
Can IS 11169 (Part 1) 42Cr4Mo2 be substituted with BS 970 (Part 1) 708M40?
IS 11169 (Part 1) 42Cr4Mo2 and BS 970 (Part 1) 708M40 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.