IS 11169 (Part 1):2022 42Cr4Mo2S3 Steel: Specifications & Listings
IS 11169 (Part 1):2022 42Cr4Mo2S3: Cold heading quality alloy steel 42Cr4Mo2S3 to IS 11169 (Part 1):2022 for quenching and tempering after cold heading or cold extrusion, supplied as wire rod, bars or wire of 2 to 100 mm. Maximum tensile strength annealed is 630 MPa. It can be ordered with hardenability requirements (H, HH or HL, CH).
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C
Cr
Cu
Mn
Mo
P
S
Si
0.38-0.45
0.90-1.20
<=0.25
0.60-0.90
0.15-0.30
<=0.025
0.020-0.040
<=0.30
Mechanical Properties
Core Hardness (CH)
>=50 HRC up to 21 mm
Tensile Strength, annealed (+AC)
<=630 MPa (over 5 to 40 mm)
More data from IS 11169 (Part 1):2022
From the standard
Other composition limitsfrom the table notes and clauses
Values
Maximum unless a range is given (ladle analysis)
Silicon
Lower silicon contents may be agreed when ordering, with due regard to the effect on properties such as hardenability
Ordered with hardenability
Small deviations from these limits are allowed (not for sulphur and phosphorus): up to 0.01 percent for carbon and the Table 1 values for other elements
Deoxidation
Aluminium killed (clause 6.2)
Elements not listed are not added intentionally without the purchaser's agreement, except those used to finish the heat.
Source: IS 11169 (Part 1):2022, Table C.2 and its notes, clause 6.2
Tensile strength and reduction of area by delivery conditionby delivery condition and size
Delivery condition
Diameter (mm)
Tensile strength, max (MPa)
Reduction of area, min (%)
+AC or +AC+PE
over 5 to 40
630
58
+AC+C+AC
2 (incl.) to 5
620
60
+AC+C+AC
over 5 to 40
610
60
+AC+C+AC+LC
2 (incl.) to 5
660
58
+AC+C+AC+LC
over 5 to 40
650
58
Codes: +AR as hot rolled, +PE peeled, +C cold drawn, +AC annealed to spheroidized carbides, +LC skin passed. For non-circular sections the properties are agreed between manufacturer and purchaser.
Source: IS 11169 (Part 1):2022, Table C.5
Hardenability, end quench test (H)Hardness band
Hardness band (HRC, minimum to maximum) by distance from the quenched end (mm)
1.5
3
5
7
9
11
13
15
20
25
30
35
40
45
50
Distance from quenched end (mm)
1.5
3
5
7
9
11
13
15
20
25
30
35
40
45
50
Maximum, HRC
61
61
61
60
60
59
59
58
56
53
51
48
47
46
45
Minimum, HRC
53
53
52
51
49
43
40
37
34
32
31
30
30
29
29
Applies when ordered with the symbol H; otherwise for guidance only. Jominy test as per IS 3848, austenitizing at 850 ± 5 °C.
Source: IS 11169 (Part 1):2022, Table C.9
Restricted hardenability bands, HH and HL (HRC by distance from quenched end, mm)HH and HL ordering
Band
1.5
3
5
7
9
11
13
15
20
25
30
35
40
45
50
HH maximum
61
61
61
60
60
59
59
58
56
53
51
48
47
46
45
HH minimum
56
56
55
54
52
48
46
44
41
39
38
36
36
35
34
HL maximum
58
58
58
57
56
54
53
51
49
46
44
42
41
40
40
HL minimum
53
53
52
51
49
43
40
37
34
32
31
30
30
29
29
HH: the upper limit matches the H band upper limit; HL: the lower limit matches the H band lower limit. Austenitizing at 850 ± 5 °C. Not applicable to steels ordered with a restricted range of carbon content.
Source: IS 11169 (Part 1):2022, Table C.11
Core hardening (CH)CH ordering
Austenitizing temperature
850 °C ± 5
Minimum core hardness, 90 percent martensite
50 HRC
Maximum diameter for 90 percent martensite in the core
21 mm
Applies when ordered with the symbol CH. The diameter is the one reached with the lowest hardenability of the grade; HH grades allow a larger diameter. A hardening time of at least 30 minutes at temperature is recommended.
Source: IS 11169 (Part 1):2022, Table C.12, clauses 8.2.4 and 8.2.6