IS 11169 (Part 1) 4C2 vs BS 970 (Part 1) 060A32

Minimal Match — 35% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 1) 4C2 (IS 11169 (Part 1):2022) and BS 970 (Part 1) 060A32 (BS 970 (Part 1):1983) are both steel grades. Both fall under the Carbon Steel category. IS 11169 (Part 1) 4C2 is typically used for cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex a), while BS 970 (Part 1) 060A32 is commonly used for through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of table 6.. IS 11169 (Part 1) 4C2 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 060A32 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 11169 (Part 1) 4C2 vs BS 970 (Part 1) 060A32 is a 70.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a minimal match overall at 35%.

Frequently Compared With IS 11169 (Part 1) 4C2:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 080A20 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045M10 BS 970 (Part 3) 045A10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A04 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045M10
Match Breakdown
CHEMISTRY MATCH
70.7%
MECHANICAL MATCH
No shared data
OVERALL
35%
Specifications
Property IS 11169 (Part 1) 4C2 BS 970 (Part 1) 060A32
Standard IS 11169 (Part 1):2022 BS 970 (Part 1):1983
Category Carbon Steel Carbon Steel
C (%) <=0.08 0.30-0.35
Cr (%) <=0.15 Not specified
Cu (%) <=0.15 Not specified
Mn (%) <=0.40 0.50-0.70
Mo (%) <=0.05 Not specified
Ni (%) <=0.15 Not specified
P (%) <=0.035 <=0.050
S (%) <=0.035 <=0.050
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 1) 4C2 BS 970 (Part 1) 060A32
Hardness, annealed (+AC) <=120 HBW Not specified
Typical Applications
IS 11169 (Part 1) 4C2
Cold heading and cold extrusion of parts not heat treated after cold forming; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex A)
BS 970 (Part 1) 060A32
Through hardening steel for mechanical and allied engineering purposes; supplied in the hardened and tempered conditions of Table 6.
Key Differences
Can IS 11169 (Part 1) 4C2 Be Substituted With BS 970 (Part 1) 060A32?
IS 11169 (Part 1) 4C2 and BS 970 (Part 1) 060A32 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 1) 4C2
0 active listings and RFQs →
BS 970 (Part 1) 060A32
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 1) 4C2 and BS 970 (Part 1) 060A32?
IS 11169 (Part 1) 4C2 specifies Cr, Cu, Mo, Ni which are not specified for BS 970 (Part 1) 060A32.
Can IS 11169 (Part 1) 4C2 be substituted with BS 970 (Part 1) 060A32?
IS 11169 (Part 1) 4C2 and BS 970 (Part 1) 060A32 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.