IS 11169 (Part 1) 30Ni13Cr5 vs IS 11169 (Part 1) 15Ni5Cr5
Close Alternative — 84.9% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 1) 30Ni13Cr5 (IS 11169 (Part 1):1984) and IS 11169 (Part 1) 15Ni5Cr5 (IS 11169 (Part 1):2022) are both steel grades.
Both fall under the Alloy Steel category.
IS 11169 (Part 1) 30Ni13Cr5 is typically used for heavy shafts, axles, connecting rods, large gears, structural components in mining and construction equipment., while IS 11169 (Part 1) 15Ni5Cr5 is commonly used for cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, annex b).
IS 11169 (Part 1) 30Ni13Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 15Ni5Cr5 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 1) 30Ni13Cr5 vs IS 11169 (Part 1) 15Ni5Cr5 is a 84% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a close alternative overall at 84.9%.
Frequently Compared With IS 11169 (Part 1) 30Ni13Cr5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 1) 30Ni13Cr5
IS 11169 (Part 1) 15Ni5Cr5
Hardness, annealed
<=200 HB
Not specified
Hardness, annealed (+AC)
Not specified
<=200 HBW
Typical Applications
IS 11169 (Part 1) 30Ni13Cr5
Heavy shafts, axles, connecting rods, large gears, structural components in mining and construction equipment.
IS 11169 (Part 1) 15Ni5Cr5
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
IS 11169 (Part 1) 15Ni5Cr5 specifies Cu, Mo, P, S which are not specified for IS 11169 (Part 1) 30Ni13Cr5.
Can IS 11169 (Part 1) 30Ni13Cr5 Be Substituted With IS 11169 (Part 1) 15Ni5Cr5?
IS 11169 (Part 1) 30Ni13Cr5 and IS 11169 (Part 1) 15Ni5Cr5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 11169 (Part 1) 30Ni13Cr5 and IS 11169 (Part 1) 15Ni5Cr5?
IS 11169 (Part 1) 15Ni5Cr5 specifies Cu, Mo, P, S which are not specified for IS 11169 (Part 1) 30Ni13Cr5.
Can IS 11169 (Part 1) 30Ni13Cr5 be substituted with IS 11169 (Part 1) 15Ni5Cr5?
IS 11169 (Part 1) 30Ni13Cr5 and IS 11169 (Part 1) 15Ni5Cr5 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.