IS 11169 (Part 2) X04Cr17Ni12Mo2 vs GOST 5632 08X18H10
Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr17Ni12Mo2 (IS 11169 (Part 2):1989) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr17Ni12Mo2 is typically used for cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 11169 (Part 2) X04Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X04Cr17Ni12Mo2 vs GOST 5632 08X18H10 is a 64.2% match.
As per mechanical properties, the match is 33.3%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 2) X04Cr17Ni12Mo2:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr17Ni12Mo2
GOST 5632 08X18H10
Yield Strength (0.2% proof)
>=205 MPa
Not specified
Tensile Strength
500-700 MPa
≥520 MPa
Elongation
>=45%
≥40%
Impact (U-notch 5 mm)
>=60 J
Not specified
Condition
Quenched reference test piece (Table 6 treatment)
Not specified
Yield Strength
Not specified
≥205 MPa
Typical Applications
IS 11169 (Part 2) X04Cr17Ni12Mo2
Cold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
IS 11169 (Part 2) X04Cr17Ni12Mo2 specifies Mo which is not specified for GOST 5632 08X18H10.
Can IS 11169 (Part 2) X04Cr17Ni12Mo2 Be Substituted With GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr17Ni12Mo2 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr17Ni12Mo2 and GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr17Ni12Mo2 specifies Mo which is not specified for GOST 5632 08X18H10.
Can IS 11169 (Part 2) X04Cr17Ni12Mo2 be substituted with GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr17Ni12Mo2 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.