IS 11169 (Part 2):1989 X04Cr19Ni10 Steel: Specifications & Listings

IS 11169 (Part 2):1989 X04Cr19Ni10: Cold heading quality austenitic stainless steel X04Cr19Ni10 to IS 11169 (Part 2):1989, supplied as wire, wire rod or bars and ordered on chemical composition alone or with mechanical properties. The standard was reaffirmed in 2004.

Category: Stainless Steel
Grade Details
GradeIS 11169 (Part 2):1989 X04Cr19Ni10
Standard IS 11169 (Part 2):1989
ApplicationsCold heading and cold extrusion; the standard covers wires, wire rods and bars (clause 1.1)
Equivalent / Similar Grades
Grade Standard Region Live on M-EX
IS 11169 (Part 2) X04Cr19Ni10 IS 11169 (Part 2):2023 India No activity yet
ASTM A959 308 ASTM A959:2011 USA No activity yet
Grade ComparisonCompare With a Specific Grade →
Grade Standard Match
ASTM A959 347 ASTM A959:2011 Strong Match
BS 970 (Part 3) 321S31 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 3) 347S31 BS 970 (Part 3):1991 Strong Match
BS 970 (Part 1) 321S31 BS 970 (Part 1):1983 Strong Match
BS 970 (Part 1) 347S31 BS 970 (Part 1):1983 Strong Match
ASTM A959 308 ASTM A959:2011 Strong Match
EN 10088-1 X6CrNiTi18-10 EN 10088-1:2014 Strong Match
EN 10088-1 X6CrNiNb18-10 EN 10088-1:2014 Strong Match
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Chemical Composition (%)
C Si Mn Ni Cr S P
<=0.08 <=1.0 <=2.0 10.5-12.0 17.0-20.0 <=0.030 <=0.045
Mechanical Properties
Yield Strength (0.2% proof) >=185 MPa
Tensile Strength 500-700 MPa
Elongation >=50%
Impact (U-notch 5 mm) >=60 J
Condition Quenched reference test piece (Table 6 treatment)

More data from IS 11169 (Part 2):1989

From the standard
Properties in the delivery condition 3 conditions
Delivery conditionTensile strength, max (MPa)Reduction of area, min (%)
Quenched (Q), or quenched and peeled (Q+P)68055
Cold drawn and quenched (C+Q)68055
Cold drawn, quenched and lightly cold reduced (C+Q+LC)73055
Lightly cold reduced means, for example, a reduction of 5 percent. Table 4 prints the third condition as E+Q+LC; clause 10.2 gives C+Q+LC.
Source: IS 11169 (Part 2):1989, Table 4, clauses 8.1 and 10
Heat treatment of reference test pieces 1 value
Quenching temperature
1000 to 1050 °C
Treatment for the test pieces on which the mechanical properties are checked when ordered to requirement class 2 (clause 8.2).
Source: IS 11169 (Part 2):1989, Table 6

Active IS 11169 (Part 2):1989 X04Cr19Ni10 Listings on M-EX (For Sale)

+ Create a Listing for this grade

No active IS 11169 (Part 2):1989 X04Cr19Ni10 listings at this time.

Register for Alerts

Buyer RFQs for IS 11169 (Part 2):1989 X04Cr19Ni10

+ Post an RFQ for this grade

No open buyer requirements for IS 11169 (Part 2):1989 X04Cr19Ni10 at this time.

Register for Alerts