IS 11169 (Part 2) X02Cr17Ni12Mo2 vs IS 11169 (Part 2) X02Cr17Ni12Mo3

Strong Match — 95.4% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni12Mo2 (IS 11169 (Part 2):2023) and IS 11169 (Part 2) X02Cr17Ni12Mo3 (IS 11169 (Part 2):2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni12Mo2 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while IS 11169 (Part 2) X02Cr17Ni12Mo3 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11). IS 11169 (Part 2) X02Cr17Ni12Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 2) X02Cr17Ni12Mo3 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni12Mo2 vs IS 11169 (Part 2) X02Cr17Ni12Mo3 is a 93.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a strong match overall at 95.4%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni12Mo2:
GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12MoVH GOST 5632 12Kh13 EN 10088-1 1.4006 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH
Match Breakdown
CHEMISTRY MATCH
93.1%
MECHANICAL MATCH
100%
OVERALL
95.4%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 IS 11169 (Part 2) X02Cr17Ni12Mo3
Standard IS 11169 (Part 2):2023 IS 11169 (Part 2):2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 16.5-18.5 16.5-18.5
Cu (%) <=1.00 <=1.00
Mn (%) <=2.00 <=2.00
Mo (%) 2.00-3.00 2.50-3.00
N (%) <=0.10 <=0.10
Ni (%) 10.0-13.0 10.5-13.0
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni12Mo2 IS 11169 (Part 2) X02Cr17Ni12Mo3
Reduction of Area, solution annealed (+AT) >=68% (over 5 to 50 mm) >=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT) <=650 MPa (over 5 to 50 mm) <=650 MPa (over 5 to 50 mm)
Typical Applications
IS 11169 (Part 2) X02Cr17Ni12Mo2
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
IS 11169 (Part 2) X02Cr17Ni12Mo3
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 Be Substituted With IS 11169 (Part 2) X02Cr17Ni12Mo3?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and IS 11169 (Part 2) X02Cr17Ni12Mo3 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr17Ni12Mo3 is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni12Mo2
0 active listings and RFQs →
IS 11169 (Part 2) X02Cr17Ni12Mo3
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni12Mo2 and IS 11169 (Part 2) X02Cr17Ni12Mo3?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X02Cr17Ni12Mo2 be substituted with IS 11169 (Part 2) X02Cr17Ni12Mo3?
IS 11169 (Part 2) X02Cr17Ni12Mo2 and IS 11169 (Part 2) X02Cr17Ni12Mo3 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr17Ni12Mo3 is often considered as a substitute for IS 11169 (Part 2) X02Cr17Ni12Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.