IS 11169 (Part 2) X02Cr17Ni12Mo3N vs GOST 5632 12Kh13

Minimal Match — 30.4% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr17Ni12Mo3N (IS 11169 (Part 2):2023) and GOST 5632 12Kh13 (GOST 5632-2014) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr17Ni12Mo3N is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while GOST 5632 12Kh13 is commonly used for turbine blades, pump shafts, fasteners, cutlery. IS 11169 (Part 2) X02Cr17Ni12Mo3N is defined under Bureau of Indian Standards (IS) (India).

As per chemical composition, IS 11169 (Part 2) X02Cr17Ni12Mo3N vs GOST 5632 12Kh13 is a 45.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 30.4%.

Frequently Compared With IS 11169 (Part 2) X02Cr17Ni12Mo3N:
EN 10088-1 1.4845 GOST 5632 06Kh23N28 GOST 5632 08X18H10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH IS 1570 (Part 7) 12Cr12Ni2Mo GB/T 3280 06Cr19Ni10 IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
45.6%
MECHANICAL MATCH
0%
OVERALL
30.4%
Specifications
Property IS 11169 (Part 2) X02Cr17Ni12Mo3N GOST 5632 12Kh13
Standard IS 11169 (Part 2):2023 GOST 5632-2014
Category Stainless Steel Stainless Steel
C (%) <=0.030 0.09–0.15
Cr (%) 16.5-18.5 12.0–14.0
Cu (%) <=1.00 Not specified
Mn (%) <=2.00 ≤0.80
Mo (%) 2.50-3.00 Not specified
N (%) 0.12-0.22 Not specified
Ni (%) 10.5-13.0 ≤0.60
P (%) <=0.045 Not specified
S (%) <=0.015 Not specified
Si (%) <=1.00 ≤0.80
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr17Ni12Mo3N GOST 5632 12Kh13
Reduction of Area, solution annealed (+AT) >=60% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=780 MPa (over 5 to 50 mm) Not specified
Tensile Strength Not specified ≥540 MPa (annealed)
Hardness HRC Not specified 36–45 (hardened)
Typical Applications
IS 11169 (Part 2) X02Cr17Ni12Mo3N
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
GOST 5632 12Kh13
Turbine blades, pump shafts, fasteners, cutlery
Key Differences
Can IS 11169 (Part 2) X02Cr17Ni12Mo3N Be Substituted With GOST 5632 12Kh13?
IS 11169 (Part 2) X02Cr17Ni12Mo3N and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 11169 (Part 2) X02Cr17Ni12Mo3N
No active listings currently.
GOST 5632 12Kh13
Sheet → (2 listings)
Thickness: 6–6 mm (0.24–0.24 in)
Width: 1250–1250 mm (49.21–49.21 in)
Length: 2700–3400 mm (106.3–133.86 in)
On M-EX Right Now
IS 11169 (Part 2) X02Cr17Ni12Mo3N
0 active listings and RFQs →
GOST 5632 12Kh13
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr17Ni12Mo3N and GOST 5632 12Kh13?
IS 11169 (Part 2) X02Cr17Ni12Mo3N specifies Cu, Mo, N, P which are not specified for GOST 5632 12Kh13.
Can IS 11169 (Part 2) X02Cr17Ni12Mo3N be substituted with GOST 5632 12Kh13?
IS 11169 (Part 2) X02Cr17Ni12Mo3N and GOST 5632 12Kh13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.