IS 11169 (Part 2) X02Cr19Ni11 vs IS 11169 (Part 2) X02Cr19Ni9
Strong Match — 92.2% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X02Cr19Ni11 (IS 11169 (Part 2):2023) and IS 11169 (Part 2) X02Cr19Ni9 (IS 11169 (Part 2):2023) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X02Cr19Ni11 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while IS 11169 (Part 2) X02Cr19Ni9 is commonly used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11).
IS 11169 (Part 2) X02Cr19Ni11 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 2) X02Cr19Ni9 is defined under Bureau of Indian Standards (IS), originating from India.
As per chemical composition, IS 11169 (Part 2) X02Cr19Ni11 vs IS 11169 (Part 2) X02Cr19Ni9 is a 88.3% match.
As per mechanical properties, the match is 100%.
Combined, this makes them a strong match overall at 92.2%.
Frequently Compared With IS 11169 (Part 2) X02Cr19Ni11:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X02Cr19Ni11
IS 11169 (Part 2) X02Cr19Ni9
Reduction of Area, solution annealed (+AT)
>=68% (over 5 to 50 mm)
>=68% (over 5 to 50 mm)
Tensile Strength, solution annealed (+AT)
<=630 MPa (over 5 to 50 mm)
<=630 MPa (over 5 to 50 mm)
Typical Applications
IS 11169 (Part 2) X02Cr19Ni11
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
IS 11169 (Part 2) X02Cr19Ni9
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
Can IS 11169 (Part 2) X02Cr19Ni11 Be Substituted With IS 11169 (Part 2) X02Cr19Ni9?
IS 11169 (Part 2) X02Cr19Ni11 and IS 11169 (Part 2) X02Cr19Ni9 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr19Ni9 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 11169 (Part 2) X02Cr19Ni11 and IS 11169 (Part 2) X02Cr19Ni9?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X02Cr19Ni11 be substituted with IS 11169 (Part 2) X02Cr19Ni9?
IS 11169 (Part 2) X02Cr19Ni11 and IS 11169 (Part 2) X02Cr19Ni9 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 2) X02Cr19Ni9 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni11 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.