IS 11169 (Part 2) X02Cr19Ni9 vs EN 10088-1 X2CrNi18-9

Strong Match — 94.3% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X02Cr19Ni9 (IS 11169 (Part 2):2023) and EN 10088-1 X2CrNi18-9 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X02Cr19Ni9 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X2CrNi18-9 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X02Cr19Ni9 vs EN 10088-1 X2CrNi18-9 is a 94.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 94.3%.

Frequently Compared With IS 11169 (Part 2) X02Cr19Ni9:
ASTM A959 201LN GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H GOST 5632 06Kh23N28 GOST 5632 08X18H10 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr12MoVH
Match Breakdown
CHEMISTRY MATCH
94.3%
MECHANICAL MATCH
No shared data
OVERALL
94.3%
Specifications
Property IS 11169 (Part 2) X02Cr19Ni9 EN 10088-1 X2CrNi18-9
Standard IS 11169 (Part 2):2023 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.030 <=0.030
Cr (%) 17.5-19.5 17.5-19.5
Cu (%) <=1.00 Not specified
Mn (%) <=2.00 <=2.00
N (%) <=0.10 <=0.10
Ni (%) 8.0-10.0 8.0-10.5
P (%) <=0.045 <=0.045
S (%) <=0.030 <=0.015
Si (%) <=1.00 <=1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X02Cr19Ni9 EN 10088-1 X2CrNi18-9
Reduction of Area, solution annealed (+AT) >=68% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=630 MPa (over 5 to 50 mm) Not specified
Typical Applications
IS 11169 (Part 2) X02Cr19Ni9
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 X2CrNi18-9
Not documented
Key Differences
Can IS 11169 (Part 2) X02Cr19Ni9 Be Substituted With EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr19Ni9 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni9 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X02Cr19Ni9
0 active listings and RFQs →
EN 10088-1 X2CrNi18-9
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X02Cr19Ni9 and EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr19Ni9 specifies Cu which is not specified for EN 10088-1 X2CrNi18-9.
Can IS 11169 (Part 2) X02Cr19Ni9 be substituted with EN 10088-1 X2CrNi18-9?
IS 11169 (Part 2) X02Cr19Ni9 and EN 10088-1 X2CrNi18-9 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X2CrNi18-9 is often considered as a substitute for IS 11169 (Part 2) X02Cr19Ni9 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.