IS 11169 (Part 2) X04Cr17Mo1 vs EN 10088-1 X6CrMoS17
Close Alternative — 84.9% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) and EN 10088-1 X6CrMoS17 (EN 10088-1:2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X6CrMoS17 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 11169 (Part 2) X04Cr17Mo1 vs EN 10088-1 X6CrMoS17 is a 85.2% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a close alternative overall at 84.9%.
Frequently Compared With IS 11169 (Part 2) X04Cr17Mo1:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr17Mo1
EN 10088-1 X6CrMoS17
Reduction of Area, soft annealed (+A)
>=60% (over 5 to 25 mm)
Not specified
Tensile Strength, soft annealed (+A)
<=600 MPa (over 5 to 25 mm)
Not specified
Typical Applications
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
EN 10088-1 X6CrMoS17
Not documented
Can IS 11169 (Part 2) X04Cr17Mo1 Be Substituted With EN 10088-1 X6CrMoS17?
IS 11169 (Part 2) X04Cr17Mo1 and EN 10088-1 X6CrMoS17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
What is the difference between IS 11169 (Part 2) X04Cr17Mo1 and EN 10088-1 X6CrMoS17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X04Cr17Mo1 be substituted with EN 10088-1 X6CrMoS17?
IS 11169 (Part 2) X04Cr17Mo1 and EN 10088-1 X6CrMoS17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.