IS 11169 (Part 2) X04Cr17Mo1 vs EN 10088-1 X6CrMoS17

Close Alternative — 84.9% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X04Cr17Mo1 (IS 11169 (Part 2):2023) and EN 10088-1 X6CrMoS17 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X04Cr17Mo1 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X6CrMoS17 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X04Cr17Mo1 vs EN 10088-1 X6CrMoS17 is a 85.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 84.9%.

Frequently Compared With IS 11169 (Part 2) X04Cr17Mo1:
GOST 5632 08X18H10 EN 10088-1 1.4301 IS 1570 (Part 7) 12Cr12MoH GOST 5632 12Kh13 ASTM A959 .- GOST 5632 06Kh23N28 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr12Ni2Mo IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 EN 10088-1 1.4006
Match Breakdown
CHEMISTRY MATCH
85.2%
MECHANICAL MATCH
No shared data
OVERALL
84.9%
Specifications
Property IS 11169 (Part 2) X04Cr17Mo1 EN 10088-1 X6CrMoS17
Standard IS 11169 (Part 2):2023 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) <=0.08 <=0.08
Cr (%) 16.0-18.0 16.0-18.0
Mn (%) <=1.00 <=1.50
Mo (%) 0.75-1.40 0.20-0.60
P (%) <=0.040 <=0.040
S (%) <=0.030 0.15-0.35
Si (%) <=1.00 <=1.50
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X04Cr17Mo1 EN 10088-1 X6CrMoS17
Reduction of Area, soft annealed (+A) >=60% (over 5 to 25 mm) Not specified
Tensile Strength, soft annealed (+A) <=600 MPa (over 5 to 25 mm) Not specified
Typical Applications
IS 11169 (Part 2) X04Cr17Mo1
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 25 mm (clause 1.1, Table 13)
EN 10088-1 X6CrMoS17
Not documented
Can IS 11169 (Part 2) X04Cr17Mo1 Be Substituted With EN 10088-1 X6CrMoS17?
IS 11169 (Part 2) X04Cr17Mo1 and EN 10088-1 X6CrMoS17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 11169 (Part 2) X04Cr17Mo1
0 active listings and RFQs →
EN 10088-1 X6CrMoS17
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X04Cr17Mo1 and EN 10088-1 X6CrMoS17?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X04Cr17Mo1 be substituted with EN 10088-1 X6CrMoS17?
IS 11169 (Part 2) X04Cr17Mo1 and EN 10088-1 X6CrMoS17 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.