IS 11169 (Part 2) X04Cr18Ni9Cu vs GOST 5632 08X18H10
Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X04Cr18Ni9Cu (IS 11169 (Part 2):2023) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X04Cr18Ni9Cu is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 11169 (Part 2) X04Cr18Ni9Cu is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X04Cr18Ni9Cu vs GOST 5632 08X18H10 is a 75.1% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 2) X04Cr18Ni9Cu:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X04Cr18Ni9Cu
GOST 5632 08X18H10
Reduction of Area, cold drawn and solution annealed (+AT+C+AT)
>=60% (0.8 to 5 mm) / >=65% (over 5 to 25 mm)
Not specified
Tensile Strength, cold drawn and solution annealed (+AT+C+AT)
<=710 MPa (0.8 to 2 mm) / <=700 MPa (over 2 to 5 mm) / <=650 MPa (over 5 to 25 mm)
Not specified
Tensile Strength
Not specified
≥520 MPa
Yield Strength
Not specified
≥205 MPa
Elongation
Not specified
≥40%
Typical Applications
IS 11169 (Part 2) X04Cr18Ni9Cu
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Key Differences
IS 11169 (Part 2) X04Cr18Ni9Cu specifies Cu, N which are not specified for GOST 5632 08X18H10.
Can IS 11169 (Part 2) X04Cr18Ni9Cu Be Substituted With GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr18Ni9Cu and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X04Cr18Ni9Cu and GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr18Ni9Cu specifies Cu, N which are not specified for GOST 5632 08X18H10.
Can IS 11169 (Part 2) X04Cr18Ni9Cu be substituted with GOST 5632 08X18H10?
IS 11169 (Part 2) X04Cr18Ni9Cu and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.