IS 11169 (Part 2) X10Cr18Ni8 vs ASTM A959 XM-2

Related Material — 69% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X10Cr18Ni8 (IS 11169 (Part 2):2023) and ASTM A959 XM-2 (ASTM A959:2011) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X10Cr18Ni8 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, table 11), while ASTM A959 XM-2 is commonly used for wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1). IS 11169 (Part 2) X10Cr18Ni8 is defined under Bureau of Indian Standards (IS), originating from India, while ASTM A959 XM-2 is defined under ASTM International, originating from United States.

As per chemical composition, IS 11169 (Part 2) X10Cr18Ni8 vs ASTM A959 XM-2 is a 69% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69%.

Frequently Compared With IS 11169 (Part 2) X10Cr18Ni8:
IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH IS 1570 (Part 7) 12Cr13H
Match Breakdown
CHEMISTRY MATCH
69%
MECHANICAL MATCH
No shared data
OVERALL
69%
Specifications
Property IS 11169 (Part 2) X10Cr18Ni8 ASTM A959 XM-2
Standard IS 11169 (Part 2):2023 ASTM A959:2011
Category Stainless Steel Stainless Steel
C (%) 0.05-0.15 <=0.15
Cr (%) 16.0-19.0 17.0-19.0
Cu (%) <=1.00 Not specified
Mn (%) <=2.00 <=2.00
Mo (%) <=0.80 0.40-0.60
N (%) <=0.10 Not specified
Ni (%) 6.0-9.5 8.0-10.0
P (%) <=0.045 <=0.05
S (%) <=0.015 0.11-0.16
Si (%) <=2.00 <=1.00
Al (%) Not specified 0.60-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X10Cr18Ni8 ASTM A959 XM-2
Reduction of Area, solution annealed (+AT) >=65% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=660 MPa (over 5 to 50 mm) Not specified
Typical Applications
IS 11169 (Part 2) X10Cr18Ni8
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
ASTM A959 XM-2
Wrought stainless steel products; recommended composition limits for adoption by product standards (clause 1.1)
Key Differences
Can IS 11169 (Part 2) X10Cr18Ni8 Be Substituted With ASTM A959 XM-2?
IS 11169 (Part 2) X10Cr18Ni8 and ASTM A959 XM-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 11169 (Part 2) X10Cr18Ni8
0 active listings and RFQs →
ASTM A959 XM-2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X10Cr18Ni8 and ASTM A959 XM-2?
IS 11169 (Part 2) X10Cr18Ni8 specifies Cu, N which are not specified for ASTM A959 XM-2. ASTM A959 XM-2 specifies Al which is not specified for IS 11169 (Part 2) X10Cr18Ni8.
Can IS 11169 (Part 2) X10Cr18Ni8 be substituted with ASTM A959 XM-2?
IS 11169 (Part 2) X10Cr18Ni8 and ASTM A959 XM-2 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.