IS 11169 (Part 2) X10Cr18Ni8 vs EN 10088-1 X10CrNi18-8

Strong Match — 96% match based on chemical composition and mechanical property overlap.

IS 11169 (Part 2) X10Cr18Ni8 (IS 11169 (Part 2):2023) and EN 10088-1 X10CrNi18-8 (EN 10088-1:2023) are both steel grades. Both fall under the Stainless Steel category. IS 11169 (Part 2) X10Cr18Ni8 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10088-1 X10CrNi18-8 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 11169 (Part 2) X10Cr18Ni8 vs EN 10088-1 X10CrNi18-8 is a 96% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 96%.

Frequently Compared With IS 11169 (Part 2) X10Cr18Ni8:
IS 1570 (Part 7) 12Cr12Ni2Mo GOST 5632 12Kh13 GOST 5632 08X18H10 EN 10088-1 1.4301 EN 10088-1 1.4401 EN 10088-1 1.4845 IS 1570 (Part 7) 12Cr13H GB/T 3280 06Cr19Ni10 GOST 5632 06Kh23N28 EN 10088-1 1.4006 IS 1570 (Part 7) 11Cr17Ni13W3TiH IS 1570 (Part 7) 12Cr12MoH
Match Breakdown
CHEMISTRY MATCH
96%
MECHANICAL MATCH
No shared data
OVERALL
96%
Specifications
Property IS 11169 (Part 2) X10Cr18Ni8 EN 10088-1 X10CrNi18-8
Standard IS 11169 (Part 2):2023 EN 10088-1:2023
Category Stainless Steel Stainless Steel
C (%) 0.05-0.15 0.030-0.15
Cr (%) 16.0-19.0 16.0-19.0
Cu (%) <=1.00 Not specified
Mn (%) <=2.00 <=2.00
Mo (%) <=0.80 <=0.80
N (%) <=0.10 <=0.10
Ni (%) 6.0-9.5 6.0-9.5
P (%) <=0.045 <=0.045
S (%) <=0.015 <=0.015
Si (%) <=2.00 <=2.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 11169 (Part 2) X10Cr18Ni8 EN 10088-1 X10CrNi18-8
Reduction of Area, solution annealed (+AT) >=65% (over 5 to 50 mm) Not specified
Tensile Strength, solution annealed (+AT) <=660 MPa (over 5 to 50 mm) Not specified
Typical Applications
IS 11169 (Part 2) X10Cr18Ni8
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 50 mm (clause 1.1, Table 11)
EN 10088-1 X10CrNi18-8
Not documented
Key Differences
Can IS 11169 (Part 2) X10Cr18Ni8 Be Substituted With EN 10088-1 X10CrNi18-8?
IS 11169 (Part 2) X10Cr18Ni8 and EN 10088-1 X10CrNi18-8 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X10CrNi18-8 is often considered as a substitute for IS 11169 (Part 2) X10Cr18Ni8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 11169 (Part 2) X10Cr18Ni8
0 active listings and RFQs →
EN 10088-1 X10CrNi18-8
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 11169 (Part 2) X10Cr18Ni8 and EN 10088-1 X10CrNi18-8?
IS 11169 (Part 2) X10Cr18Ni8 specifies Cu which is not specified for EN 10088-1 X10CrNi18-8.
Can IS 11169 (Part 2) X10Cr18Ni8 be substituted with EN 10088-1 X10CrNi18-8?
IS 11169 (Part 2) X10Cr18Ni8 and EN 10088-1 X10CrNi18-8 overlap closely enough on chemistry and mechanical properties that EN 10088-1 X10CrNi18-8 is often considered as a substitute for IS 11169 (Part 2) X10Cr18Ni8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.