Minimal Match — 35% match
based on chemical composition and mechanical property overlap.
IS 11169 (Part 2) X12Cr13 (IS 11169 (Part 2):2023) and GOST 5632 08X18H10 (GOST 5632-2014) are both steel grades.
Both fall under the Stainless Steel category.
IS 11169 (Part 2) X12Cr13 is typically used for cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 100 mm (clause 1.1, table 14), while GOST 5632 08X18H10 is commonly used for chemical equipment, food processing, general corrosion resistant applications.
IS 11169 (Part 2) X12Cr13 is defined under Bureau of Indian Standards (IS) (India).
As per chemical composition, IS 11169 (Part 2) X12Cr13 vs GOST 5632 08X18H10 is a 62.7% match.
As per mechanical properties, the match is 0%.
Combined, this makes them a minimal match overall at 35%.
Frequently Compared With IS 11169 (Part 2) X12Cr13:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 11169 (Part 2) X12Cr13
GOST 5632 08X18H10
Reduction of Area, soft annealed (+A)
>=60% (over 5 to 100 mm)
Not specified
Tensile Strength, soft annealed (+A)
<=600 MPa (over 5 to 100 mm)
Not specified
Tensile Strength
Not specified
≥520 MPa
Yield Strength
Not specified
≥205 MPa
Elongation
Not specified
≥40%
Typical Applications
IS 11169 (Part 2) X12Cr13
Cold heading and cold extrusion of stainless steel parts; the standard covers wires, wire rods and bars of 0.8 to 100 mm (clause 1.1, Table 14)
GOST 5632 08X18H10
Chemical equipment, food processing, general corrosion resistant applications
Can IS 11169 (Part 2) X12Cr13 Be Substituted With GOST 5632 08X18H10?
IS 11169 (Part 2) X12Cr13 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
What is the difference between IS 11169 (Part 2) X12Cr13 and GOST 5632 08X18H10?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 11169 (Part 2) X12Cr13 be substituted with GOST 5632 08X18H10?
IS 11169 (Part 2) X12Cr13 and GOST 5632 08X18H10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.