IS 1570 (Part 2/Sec 1) 25C8 vs BS 970 (Part 3) 045A10

Close Alternative — 80% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 25C8 (IS 1570 (Part 2/Sec 1):1979) and BS 970 (Part 3) 045A10 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 25C8 is typically used for billets and bars for forgings, carbon steel forgings, flame and induction hardened parts, hardened and tempered parts and welded round link chains (the standard links this grade to is 1875, is 2004, is 3930, is 5517, is 6967), while BS 970 (Part 3) 045A10 is commonly used for bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (table 14). IS 1570 (Part 2/Sec 1) 25C8 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 045A10 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 2/Sec 1) 25C8 vs BS 970 (Part 3) 045A10 is a 80% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 25C8:
BS 970 (Part 1) 070M26 BS 970 (Part 1) 040A10 BS 970 (Part 1) 080A20 BS 970 (Part 3) 070M55 BS 970 (Part 3) 045M10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10
Match Breakdown
CHEMISTRY MATCH
80%
MECHANICAL MATCH
No shared data
OVERALL
80%
Specifications
Property IS 1570 (Part 2/Sec 1) 25C8 BS 970 (Part 3) 045A10
Standard IS 1570 (Part 2/Sec 1):1979 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.20-0.30 0.08-0.13
Mn (%) 0.60-0.90 0.30-0.60
Si (%) Not specified 0.10-0.40
P (%) Not specified <=0.05
S (%) Not specified <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 25C8 BS 970 (Part 3) 045A10
Tensile Strength 470-570 MPa Not specified
Elongation >=22% Not specified
Typical Applications
IS 1570 (Part 2/Sec 1) 25C8
Billets and bars for forgings, carbon steel forgings, flame and induction hardened parts, hardened and tempered parts and welded round link chains (the standard links this grade to IS 1875, IS 2004, IS 3930, IS 5517, IS 6967)
BS 970 (Part 3) 045A10
Bright cold finished bars (cold drawn, turned or precision ground) for general engineering purposes, in straight lengths; case hardening steel, carbon and carbon manganese (Table 14)
Key Differences
Can IS 1570 (Part 2/Sec 1) 25C8 Be Substituted With BS 970 (Part 3) 045A10?
IS 1570 (Part 2/Sec 1) 25C8 and BS 970 (Part 3) 045A10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 25C8
0 active listings and RFQs →
BS 970 (Part 3) 045A10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 25C8 and BS 970 (Part 3) 045A10?
BS 970 (Part 3) 045A10 specifies Si, P, S which are not specified for IS 1570 (Part 2/Sec 1) 25C8.
Can IS 1570 (Part 2/Sec 1) 25C8 be substituted with BS 970 (Part 3) 045A10?
IS 1570 (Part 2/Sec 1) 25C8 and BS 970 (Part 3) 045A10 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.