IS 1570 (Part 2/Sec 1) 30C8 vs BS 970 (Part 3) 070M55

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 30C8 (IS 1570 (Part 2/Sec 1):1979) and BS 970 (Part 3) 070M55 (BS 970 (Part 3):1991) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 30C8 is typically used for billets and bars for forgings, carbon steel forgings, flame and induction hardened parts, hardened and tempered parts and welded round link chains (the standard links this grade to is 1875, is 2004, is 3930, is 5517, is 6967), while BS 970 (Part 3) 070M55 is commonly used for used for springs, blades, wear plates, hand tools, shafts, and cutting components.. IS 1570 (Part 2/Sec 1) 30C8 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 3) 070M55 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 2/Sec 1) 30C8 vs BS 970 (Part 3) 070M55 is a 84.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 30C8:
BS 970 (Part 1) 080A20 BS 970 (Part 1) 040A10 BS 970 (Part 1) 040A04 BS 970 (Part 1) 045M10 BS 970 (Part 1) 055M15 BS 970 (Part 1) 040A12 BS 970 (Part 3) 045M10 BS 970 (Part 1) 060A32 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045M10 BS 970 (Part 3) 045A10
Match Breakdown
CHEMISTRY MATCH
84.3%
MECHANICAL MATCH
No shared data
OVERALL
69.9%
Specifications
Property IS 1570 (Part 2/Sec 1) 30C8 BS 970 (Part 3) 070M55
Standard IS 1570 (Part 2/Sec 1):1979 BS 970 (Part 3):1991
Category Carbon Steel Carbon Steel
C (%) 0.25-0.35 0.50-0.60
Mn (%) 0.60-0.90 0.50-0.90
Si (%) Not specified 0.10-0.40
P (%) Not specified <=0.05
S (%) Not specified <=0.05
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 30C8 BS 970 (Part 3) 070M55
Tensile Strength 500-600 MPa Not specified
Elongation >=21% Not specified
Typical Applications
IS 1570 (Part 2/Sec 1) 30C8
Billets and bars for forgings, carbon steel forgings, flame and induction hardened parts, hardened and tempered parts and welded round link chains (the standard links this grade to IS 1875, IS 2004, IS 3930, IS 5517, IS 6967)
BS 970 (Part 3) 070M55
Used for springs, blades, wear plates, hand tools, shafts, and cutting components.
Key Differences
Can IS 1570 (Part 2/Sec 1) 30C8 Be Substituted With BS 970 (Part 3) 070M55?
IS 1570 (Part 2/Sec 1) 30C8 and BS 970 (Part 3) 070M55 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 2/Sec 1) 30C8
No active listings currently.
BS 970 (Part 3) 070M55
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 4800–5800 mm (188.98–228.35 in)
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 30C8
0 active listings and RFQs →
BS 970 (Part 3) 070M55
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 30C8 and BS 970 (Part 3) 070M55?
BS 970 (Part 3) 070M55 specifies Si, P, S which are not specified for IS 1570 (Part 2/Sec 1) 30C8.
Can IS 1570 (Part 2/Sec 1) 30C8 be substituted with BS 970 (Part 3) 070M55?
IS 1570 (Part 2/Sec 1) 30C8 and BS 970 (Part 3) 070M55 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.