IS 1570 (Part 2/Sec 1) 55C8 vs SAE J403 1055

Strong Match — 100% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 2/Sec 1) 55C8 (IS 1570 (Part 2/Sec 1):1979) and SAE J403 1055 (SAE J403:2014) are both steel grades. Both fall under the Carbon Steel category. IS 1570 (Part 2/Sec 1) 55C8 is typically used for billets and bars for forgings, forged steel rolls, hardened and tempered parts and engine valves (the standard links this grade to is 1875, is 3445, is 5517, is 7494), while SAE J403 1055 is commonly used for chemistry-only grade; product scope as listed in the composition notes. IS 1570 (Part 2/Sec 1) 55C8 is defined under Bureau of Indian Standards (IS), originating from India, while SAE J403 1055 is defined under SAE International, originating from United States.

As per chemical composition, IS 1570 (Part 2/Sec 1) 55C8 vs SAE J403 1055 is a 100% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 100%.

Frequently Compared With IS 1570 (Part 2/Sec 1) 55C8:
BS 970 (Part 3) 070M55 BS 970 (Part 1) 040A10 BS 970 (Part 1) 070M55 BS 970 (Part 1) 040A04 BS 970 (Part 1) 055M15 BS 970 (Part 1) 045M10 BS 970 (Part 1) 040A12 BS 970 (Part 1) 045A10 BS 970 (Part 1) 045A10 BS 970 (Part 3) 045A10 BS 970 (Part 3) 045M10 BS 970 (Part 1) 045M10
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
No shared data
OVERALL
100%
Specifications
Property IS 1570 (Part 2/Sec 1) 55C8 SAE J403 1055
Standard IS 1570 (Part 2/Sec 1):1979 SAE J403:2014
Category Carbon Steel Carbon Steel
C (%) 0.50-0.60 0.50-0.60
Mn (%) 0.60-0.90 0.60-0.90
P (%) Not specified <=0.030 (flat rolled), <=0.040 (long products)
S (%) Not specified <=0.035 (flat rolled), <=0.050 (long products)
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 2/Sec 1) 55C8 SAE J403 1055
Tensile Strength >=720 MPa Not specified
Elongation >=13% Not specified
Typical Applications
IS 1570 (Part 2/Sec 1) 55C8
Billets and bars for forgings, forged steel rolls, hardened and tempered parts and engine valves (the standard links this grade to IS 1875, IS 3445, IS 5517, IS 7494)
SAE J403 1055
Chemistry-only grade; product scope as listed in the composition notes
Key Differences
Can IS 1570 (Part 2/Sec 1) 55C8 Be Substituted With SAE J403 1055?
IS 1570 (Part 2/Sec 1) 55C8 and SAE J403 1055 overlap closely enough on chemistry and mechanical properties that SAE J403 1055 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 55C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 1570 (Part 2/Sec 1) 55C8
No active listings currently.
SAE J403 1055
Round Bar → (2 listings)
Diameter: 40–40 mm (1.57–1.57 in)
Length: 5100–6000 mm (200.79–236.22 in)
On M-EX Right Now
IS 1570 (Part 2/Sec 1) 55C8
0 active listings and RFQs →
SAE J403 1055
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 2/Sec 1) 55C8 and SAE J403 1055?
SAE J403 1055 specifies P, S which are not specified for IS 1570 (Part 2/Sec 1) 55C8.
Can IS 1570 (Part 2/Sec 1) 55C8 be substituted with SAE J403 1055?
IS 1570 (Part 2/Sec 1) 55C8 and SAE J403 1055 overlap closely enough on chemistry and mechanical properties that SAE J403 1055 is often considered as a substitute for IS 1570 (Part 2/Sec 1) 55C8 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.