IS 1570 (Part 4) 07Cr4Mo6 vs IS 4367 07Cr4Mo6

Strong Match — 98.3% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 07Cr4Mo6 (IS 1570 (Part 4):1988) and IS 4367 07Cr4Mo6 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 07Cr4Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 07Cr4Mo6 vs IS 4367 07Cr4Mo6 is a 98.3% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 98.3%.

Frequently Compared With IS 1570 (Part 4) 07Cr4Mo6:
IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 10Mo6 NF A35-565 100C6 IS 1570 (Part 4) 10Cr20Mo6 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 1570 (Part 4) 103Cr6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 7) 12Cr2Mo5V2H
Match Breakdown
CHEMISTRY MATCH
98.3%
MECHANICAL MATCH
No shared data
OVERALL
98.3%
Specifications
Property IS 1570 (Part 4) 07Cr4Mo6 IS 4367 07Cr4Mo6
Standard IS 1570 (Part 4):1988 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) <=0.12 <=0.12
Si (%) 0.15-0.60 0.15-0.60
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) <=0.30 <=0.30
Cr (%) 0.70-1.10 0.70-1.10
Mo (%) 0.45-0.65 0.45-0.65
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 07Cr4Mo6 IS 4367 07Cr4Mo6
Tensile Strength Not specified 380-550 MPa
Yield Strength Not specified 225 MPa min
Elongation Not specified >=19%
Izod Impact Not specified 60 J min
Hardness (soft annealed) Not specified <=170 HB
Condition Not specified Normalised and tempered, ruling section up to 40 mm
Key Differences
Can IS 1570 (Part 4) 07Cr4Mo6 Be Substituted With IS 4367 07Cr4Mo6?
IS 1570 (Part 4) 07Cr4Mo6 and IS 4367 07Cr4Mo6 overlap closely enough on chemistry and mechanical properties that IS 4367 07Cr4Mo6 is often considered as a substitute for IS 1570 (Part 4) 07Cr4Mo6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 4) 07Cr4Mo6
0 active listings and RFQs →
IS 4367 07Cr4Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 07Cr4Mo6 and IS 4367 07Cr4Mo6?
IS 4367 07Cr4Mo6 specifies S, P which are not specified for IS 1570 (Part 4) 07Cr4Mo6.
Can IS 1570 (Part 4) 07Cr4Mo6 be substituted with IS 4367 07Cr4Mo6?
IS 1570 (Part 4) 07Cr4Mo6 and IS 4367 07Cr4Mo6 overlap closely enough on chemistry and mechanical properties that IS 4367 07Cr4Mo6 is often considered as a substitute for IS 1570 (Part 4) 07Cr4Mo6 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.