IS 1570 (Part 4) 13Ni13Cr3 vs EN 10084 15NiCr13

Strong Match — 85% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 13Ni13Cr3 (IS 1570 (Part 4):1988) and EN 10084 15NiCr13 (EN 10084:2008) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 13Ni13Cr3 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10084 15NiCr13 is defined under European Standard (EN), originating from Europe.

As per chemical composition, IS 1570 (Part 4) 13Ni13Cr3 vs EN 10084 15NiCr13 is a 85% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 85%.

Frequently Compared With IS 1570 (Part 4) 13Ni13Cr3:
IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 105Cr5 NF A35-565 100C6 GOST 4543 12HN3A UNI 11234 100Cr6 IS 4367 07Cr4Mo6 GB/T 3077 12CrNi2
Match Breakdown
CHEMISTRY MATCH
85%
MECHANICAL MATCH
No shared data
OVERALL
85%
Specifications
Property IS 1570 (Part 4) 13Ni13Cr3 EN 10084 15NiCr13
Standard IS 1570 (Part 4):1988 EN 10084:2008
Category Alloy Steel Alloy Steel
C (%) 0.10-0.15 0.14-0.20
Si (%) 0.15-0.35 <=0.40
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) 3.00-3.50 3.00-3.50
Cr (%) 0.60-1.00 0.60-0.90
P (%) Not specified <=0.025
S (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 13Ni13Cr3 EN 10084 15NiCr13
Tensile Strength >=840 MPa Not specified
Elongation >=12% Not specified
Izod Impact >=48 J Not specified
Condition Case hardening steel, refined and quenched, core properties Soft annealed
Hardenability Not specified +H band at 1.5 mm from the quenched end: 41 to 48 HRC
Hardness Not specified Soft annealed: 229 HB max
Typical Applications
IS 1570 (Part 4) 13Ni13Cr3
Not documented
EN 10084 15NiCr13
Heavily loaded gears, cams, camshafts
Key Differences
Can IS 1570 (Part 4) 13Ni13Cr3 Be Substituted With EN 10084 15NiCr13?
IS 1570 (Part 4) 13Ni13Cr3 and EN 10084 15NiCr13 overlap closely enough on chemistry and mechanical properties that EN 10084 15NiCr13 is often considered as a substitute for IS 1570 (Part 4) 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
Forms & Sizes Available on M-EX
IS 1570 (Part 4) 13Ni13Cr3
No active listings currently.
EN 10084 15NiCr13
Round Bar → (6 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 5200–7000 mm (204.72–275.59 in)
On M-EX Right Now
IS 1570 (Part 4) 13Ni13Cr3
0 active listings and RFQs →
EN 10084 15NiCr13
6 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 13Ni13Cr3 and EN 10084 15NiCr13?
EN 10084 15NiCr13 specifies P, S which are not specified for IS 1570 (Part 4) 13Ni13Cr3.
Can IS 1570 (Part 4) 13Ni13Cr3 be substituted with EN 10084 15NiCr13?
IS 1570 (Part 4) 13Ni13Cr3 and EN 10084 15NiCr13 overlap closely enough on chemistry and mechanical properties that EN 10084 15NiCr13 is often considered as a substitute for IS 1570 (Part 4) 13Ni13Cr3 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.