IS 1570 (Part 4) 15Ni7Cr4Mo2 vs IS 11169 (Part 1) 15Ni7Cr4Mo2

Strong Match — 95.2% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 15Ni7Cr4Mo2 (IS 1570 (Part 4):1988) and IS 11169 (Part 1) 15Ni7Cr4Mo2 (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 15Ni7Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 15Ni7Cr4Mo2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 15Ni7Cr4Mo2 vs IS 11169 (Part 1) 15Ni7Cr4Mo2 is a 95.2% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a strong match overall at 95.2%.

Frequently Compared With IS 1570 (Part 4) 15Ni7Cr4Mo2:
GOST 4543 12HN3A IS 1570 (Part 4) 07Cr4Mo6 NF A35-565 100C6 GB/T 3077 12Cr2Ni4A UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
95.2%
MECHANICAL MATCH
No shared data
OVERALL
95.2%
Specifications
Property IS 1570 (Part 4) 15Ni7Cr4Mo2 IS 11169 (Part 1) 15Ni7Cr4Mo2
Standard IS 1570 (Part 4):1988 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.12-0.18 0.12-0.18
Si (%) 0.15-0.35 0.10-0.35
Mn (%) 0.60-1.00 0.60-1.00
Ni (%) 1.50-2.00 1.50-2.00
Cr (%) 0.75-1.25 0.75-1.25
Mo (%) 0.10-0.20 0.10-0.20
Cu (%) Not specified <=0.15
P (%) Not specified <=0.035
S (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 15Ni7Cr4Mo2 IS 11169 (Part 1) 15Ni7Cr4Mo2
Tensile Strength >=1080 MPa Not specified
Elongation >=9% Not specified
Izod Impact >=35 J Not specified
Condition Case hardening steel, refined and quenched, core properties Not specified
Hardness, annealed (+AC) Not specified <=180 HBW
Typical Applications
IS 1570 (Part 4) 15Ni7Cr4Mo2
Not documented
IS 11169 (Part 1) 15Ni7Cr4Mo2
Cold heading and cold extrusion of parts that are case hardened; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex B)
Key Differences
Can IS 1570 (Part 4) 15Ni7Cr4Mo2 Be Substituted With IS 11169 (Part 1) 15Ni7Cr4Mo2?
IS 1570 (Part 4) 15Ni7Cr4Mo2 and IS 11169 (Part 1) 15Ni7Cr4Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15Ni7Cr4Mo2 is often considered as a substitute for IS 1570 (Part 4) 15Ni7Cr4Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
On M-EX Right Now
IS 1570 (Part 4) 15Ni7Cr4Mo2
0 active listings and RFQs →
IS 11169 (Part 1) 15Ni7Cr4Mo2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 15Ni7Cr4Mo2 and IS 11169 (Part 1) 15Ni7Cr4Mo2?
IS 11169 (Part 1) 15Ni7Cr4Mo2 specifies Cu, P, S which are not specified for IS 1570 (Part 4) 15Ni7Cr4Mo2.
Can IS 1570 (Part 4) 15Ni7Cr4Mo2 be substituted with IS 11169 (Part 1) 15Ni7Cr4Mo2?
IS 1570 (Part 4) 15Ni7Cr4Mo2 and IS 11169 (Part 1) 15Ni7Cr4Mo2 overlap closely enough on chemistry and mechanical properties that IS 11169 (Part 1) 15Ni7Cr4Mo2 is often considered as a substitute for IS 1570 (Part 4) 15Ni7Cr4Mo2 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.