IS 1570 (Part 4) 18C10BT vs IS 11169 (Part 1) 20C10BT (quenching and tempering)

Close Alternative — 76.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 18C10BT (IS 1570 (Part 4):1988) and IS 11169 (Part 1) 20C10BT (quenching and tempering) (IS 11169 (Part 1):2022) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 18C10BT is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 20C10BT (quenching and tempering) is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 18C10BT vs IS 11169 (Part 1) 20C10BT (quenching and tempering) is a 76.9% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 76.9%.

Frequently Compared With IS 1570 (Part 4) 18C10BT:
NF A35-565 100C6 IS 4367 07Cr4Mo6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6
Match Breakdown
CHEMISTRY MATCH
76.9%
MECHANICAL MATCH
No shared data
OVERALL
76.9%
Specifications
Property IS 1570 (Part 4) 18C10BT IS 11169 (Part 1) 20C10BT (quenching and tempering)
Standard IS 1570 (Part 4):1988 IS 11169 (Part 1):2022
Category Alloy Steel Alloy Steel
C (%) 0.15-0.20 0.18-0.23
Si (%) 0.15-0.30 <=0.30
Mn (%) 0.80-1.10 0.90-1.20
Cr (%) 0.10-0.30 <=0.30
B (%) 0.0005-0.003 0.0008-0.005
Cu (%) Not specified <=0.25
P (%) Not specified <=0.025
S (%) Not specified <=0.025
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 18C10BT IS 11169 (Part 1) 20C10BT (quenching and tempering)
Core Hardness (CH) Not specified >=39 HRC up to 14 mm
Tensile Strength, annealed (+AC) Not specified <=500 MPa (over 5 to 25 mm)
Typical Applications
IS 1570 (Part 4) 18C10BT
Not documented
IS 11169 (Part 1) 20C10BT (quenching and tempering)
Cold heading and cold extrusion of parts that are quenched and tempered; the standard covers bars, wire rods and wires of 2 to 100 mm (clause 1.1, Annex C)
Key Differences
Can IS 1570 (Part 4) 18C10BT Be Substituted With IS 11169 (Part 1) 20C10BT (quenching and tempering)?
IS 1570 (Part 4) 18C10BT and IS 11169 (Part 1) 20C10BT (quenching and tempering) are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 4) 18C10BT
0 active listings and RFQs →
IS 11169 (Part 1) 20C10BT (quenching and tempering)
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 18C10BT and IS 11169 (Part 1) 20C10BT (quenching and tempering)?
IS 11169 (Part 1) 20C10BT (quenching and tempering) specifies Cu, P, S which are not specified for IS 1570 (Part 4) 18C10BT.
Can IS 1570 (Part 4) 18C10BT be substituted with IS 11169 (Part 1) 20C10BT (quenching and tempering)?
IS 1570 (Part 4) 18C10BT and IS 11169 (Part 1) 20C10BT (quenching and tempering) are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.