Strong Match — 94.1% match
based on chemical composition and mechanical property overlap.
IS 1570 (Part 4) 20Mn5Cr5 (IS 1570 (Part 4):1988) and EN 10084 20MnCr5 (EN 10084:2008) are both steel grades.
Both fall under the Alloy Steel category.
IS 1570 (Part 4) 20Mn5Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while EN 10084 20MnCr5 is defined under European Standard (EN), originating from Europe.
As per chemical composition, IS 1570 (Part 4) 20Mn5Cr5 vs EN 10084 20MnCr5 is a 94.1% match.
Mechanical property data is not available for both grades, so this factor could not be scored.
Combined, this makes them a strong match overall at 94.1%.
Frequently Compared With IS 1570 (Part 4) 20Mn5Cr5:
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property
IS 1570 (Part 4) 20Mn5Cr5
EN 10084 20MnCr5
Tensile Strength
>=990 MPa
Not specified
Elongation
>=8%
Not specified
Izod Impact
>=38 J
Not specified
Condition
Case hardening steel, refined and quenched, core properties
Soft annealed
Hardenability
Not specified
+H band at 1.5 mm from the quenched end: 41 to 49 HRC
Hardness
Not specified
Soft annealed: 217 HB max
Typical Applications
IS 1570 (Part 4) 20Mn5Cr5
Not documented
EN 10084 20MnCr5
Gears, shafts, cams, case hardened parts
Key Differences
EN 10084 20MnCr5 specifies P, S which are not specified for IS 1570 (Part 4) 20Mn5Cr5.
Can IS 1570 (Part 4) 20Mn5Cr5 Be Substituted With EN 10084 20MnCr5?
IS 1570 (Part 4) 20Mn5Cr5 and EN 10084 20MnCr5 overlap closely enough on chemistry and mechanical properties that EN 10084 20MnCr5 is often considered as a substitute for IS 1570 (Part 4) 20Mn5Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.
What is the difference between IS 1570 (Part 4) 20Mn5Cr5 and EN 10084 20MnCr5?
EN 10084 20MnCr5 specifies P, S which are not specified for IS 1570 (Part 4) 20Mn5Cr5.
Can IS 1570 (Part 4) 20Mn5Cr5 be substituted with EN 10084 20MnCr5?
IS 1570 (Part 4) 20Mn5Cr5 and EN 10084 20MnCr5 overlap closely enough on chemistry and mechanical properties that EN 10084 20MnCr5 is often considered as a substitute for IS 1570 (Part 4) 20Mn5Cr5 in many applications. Always confirm the specific property range your application needs before substituting, and check with your supplier's mill certificate.