IS 1570 (Part 4) 30Ni16Cr5 vs IS 11169 (Part 1) 30Ni13Cr5

Related Material — 66.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 30Ni16Cr5 (IS 1570 (Part 4):1988) and IS 11169 (Part 1) 30Ni13Cr5 (IS 11169 (Part 1):1984) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 30Ni16Cr5 is defined under Bureau of Indian Standards (IS), originating from India, while IS 11169 (Part 1) 30Ni13Cr5 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 30Ni16Cr5 vs IS 11169 (Part 1) 30Ni13Cr5 is a 100% match. As per mechanical properties, the match is 0%. Combined, this makes them a related material overall at 66.7%.

Frequently Compared With IS 1570 (Part 4) 30Ni16Cr5:
NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 10Mo6 IS 1570 (Part 7) 10Mo6H GB/T 3077 12Cr2Ni4A IS 4367 07Cr4Mo6 IS 1570 (Part 7) 12Cr2Mo5V2H
Match Breakdown
CHEMISTRY MATCH
100%
MECHANICAL MATCH
0%
OVERALL
66.7%
Specifications
Property IS 1570 (Part 4) 30Ni16Cr5 IS 11169 (Part 1) 30Ni13Cr5
Standard IS 1570 (Part 4):1988 IS 11169 (Part 1):1984
Category Alloy Steel Alloy Steel
C (%) 0.26-0.34 0.26-0.34
Si (%) 0.10-0.35 0.10-0.35
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) 3.90-4.30 3.90-4.30
Cr (%) 1.10-1.40 1.10-1.40
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 30Ni16Cr5 IS 11169 (Part 1) 30Ni13Cr5
Tensile Strength >=1540 MPa Not specified
Yield Strength >=1240 MPa (0.2 % proof stress) Not specified
Elongation >=8% Not specified
Izod Impact >=14 J Not specified
Hardness >=444 HBS (guidance only) Not specified
Condition Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 150 (oil hardened) mm Not specified
Hardness, annealed Not specified <=200 HB
Typical Applications
IS 1570 (Part 4) 30Ni16Cr5
Not documented
IS 11169 (Part 1) 30Ni13Cr5
Heavy shafts, axles, connecting rods, large gears, structural components in mining and construction equipment.
Can IS 1570 (Part 4) 30Ni16Cr5 Be Substituted With IS 11169 (Part 1) 30Ni13Cr5?
IS 1570 (Part 4) 30Ni16Cr5 and IS 11169 (Part 1) 30Ni13Cr5 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
Forms & Sizes Available on M-EX
IS 1570 (Part 4) 30Ni16Cr5
No active listings currently.
IS 11169 (Part 1) 30Ni13Cr5
Round Bar → (2 listings)
Diameter: 50–50 mm (1.97–1.97 in)
Length: 4800–5900 mm (188.98–232.28 in)
On M-EX Right Now
IS 1570 (Part 4) 30Ni16Cr5
0 active listings and RFQs →
IS 11169 (Part 1) 30Ni13Cr5
2 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 30Ni16Cr5 and IS 11169 (Part 1) 30Ni13Cr5?
Both grades share a similar composition profile; see the specification table above for the exact chemistry and mechanical property values.
Can IS 1570 (Part 4) 30Ni16Cr5 be substituted with IS 11169 (Part 1) 30Ni13Cr5?
IS 1570 (Part 4) 30Ni16Cr5 and IS 11169 (Part 1) 30Ni13Cr5 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.