IS 1570 (Part 4) 35Cr5Mo6V2 vs IS 4367 10Cr9Mo10

Related Material — 64% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 35Cr5Mo6V2 (IS 1570 (Part 4):1988) and IS 4367 10Cr9Mo10 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 35Cr5Mo6V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 35Cr5Mo6V2 vs IS 4367 10Cr9Mo10 is a 64% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 64%.

Frequently Compared With IS 1570 (Part 4) 35Cr5Mo6V2:
NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 10Cr20Mo6 GOST 4543 12HN3A IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
64%
MECHANICAL MATCH
No shared data
OVERALL
64%
Specifications
Property IS 1570 (Part 4) 35Cr5Mo6V2 IS 4367 10Cr9Mo10
Standard IS 1570 (Part 4):1988 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.25-0.45 <=0.15
Si (%) 0.10-0.35 <=0.50
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) <=0.30 <=0.30
Cr (%) 1.00-1.50 2.00-2.50
Mo (%) 0.50-0.80 0.90-1.10
V (%) 0.20-0.30 Not specified
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 35Cr5Mo6V2 IS 4367 10Cr9Mo10
Tensile Strength Not specified 410-590 MPa
Yield Strength Not specified 245 MPa min
Elongation Not specified >=18%
Izod Impact Not specified 55 J min
Hardness (soft annealed) Not specified <=187 HB
Condition Not specified Normalised and tempered, ruling section up to 50 mm
Key Differences
Can IS 1570 (Part 4) 35Cr5Mo6V2 Be Substituted With IS 4367 10Cr9Mo10?
IS 1570 (Part 4) 35Cr5Mo6V2 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 4) 35Cr5Mo6V2
0 active listings and RFQs →
IS 4367 10Cr9Mo10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 35Cr5Mo6V2 and IS 4367 10Cr9Mo10?
IS 1570 (Part 4) 35Cr5Mo6V2 specifies V which is not specified for IS 4367 10Cr9Mo10. IS 4367 10Cr9Mo10 specifies S, P which are not specified for IS 1570 (Part 4) 35Cr5Mo6V2.
Can IS 1570 (Part 4) 35Cr5Mo6V2 be substituted with IS 4367 10Cr9Mo10?
IS 1570 (Part 4) 35Cr5Mo6V2 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.