IS 1570 (Part 4) 40Cr13Mo10V2 vs IS 1570 (Part 4) 15Cr13Mo6

Related Material — 69.9% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 40Cr13Mo10V2 (IS 1570 (Part 4):1988) and IS 1570 (Part 4) 15Cr13Mo6 (IS 1570 (Part 4):1988) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 40Cr13Mo10V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 1570 (Part 4) 15Cr13Mo6 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 40Cr13Mo10V2 vs IS 1570 (Part 4) 15Cr13Mo6 is a 73.1% match. As per mechanical properties, the match is 100%. Combined, this makes them a related material overall at 69.9%.

Frequently Compared With IS 1570 (Part 4) 40Cr13Mo10V2:
UNI 11234 100Cr6 NF A35-565 100C6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 103Cr4 GB/T 3077 12Cr2Ni4A GOST 4543 12HN3A IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
73.1%
MECHANICAL MATCH
100%
OVERALL
69.9%
Specifications
Property IS 1570 (Part 4) 40Cr13Mo10V2 IS 1570 (Part 4) 15Cr13Mo6
Standard IS 1570 (Part 4):1988 IS 1570 (Part 4):1988
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 0.10-0.20
Si (%) 0.10-0.35 0.15-0.35
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) <=0.30 <=0.30
Cr (%) 3.00-3.50 2.90-3.40
Mo (%) 0.90-1.10 0.45-0.65
V (%) 0.15-0.25 Not specified
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 40Cr13Mo10V2 IS 1570 (Part 4) 15Cr13Mo6
Tensile Strength >=1540 MPa >=1540 MPa
Yield Strength >=1240 MPa (0.2 % proof stress) >=1240 MPa (0.2 % proof stress)
Elongation >=8% >=8%
Izod Impact >=14 J >=14 J
Hardness >=444 HBS (guidance only) >=444 HBS (guidance only)
Condition Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 30 mm Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 63 mm
Key Differences
Can IS 1570 (Part 4) 40Cr13Mo10V2 Be Substituted With IS 1570 (Part 4) 15Cr13Mo6?
IS 1570 (Part 4) 40Cr13Mo10V2 and IS 1570 (Part 4) 15Cr13Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 4) 40Cr13Mo10V2
0 active listings and RFQs →
IS 1570 (Part 4) 15Cr13Mo6
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 40Cr13Mo10V2 and IS 1570 (Part 4) 15Cr13Mo6?
IS 1570 (Part 4) 40Cr13Mo10V2 specifies V which is not specified for IS 1570 (Part 4) 15Cr13Mo6.
Can IS 1570 (Part 4) 40Cr13Mo10V2 be substituted with IS 1570 (Part 4) 15Cr13Mo6?
IS 1570 (Part 4) 40Cr13Mo10V2 and IS 1570 (Part 4) 15Cr13Mo6 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.