Post Stock Login Register

IS 1570 (Part 4) 40Cr13Mo10V2 vs IS 4367 10Cr9Mo10

Minimal Match — 48.4% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 40Cr13Mo10V2 (IS 1570 (Part 4):1988) and IS 4367 10Cr9Mo10 (IS 4367:1991) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 40Cr13Mo10V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 4367 10Cr9Mo10 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 40Cr13Mo10V2 vs IS 4367 10Cr9Mo10 is a 72.6% match. As per mechanical properties, the match is 0%. Combined, this makes them a minimal match overall at 48.4%.

Frequently Compared With IS 1570 (Part 4) 40Cr13Mo10V2:
UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 NF A35-565 100C6 GOST 4543 12HN3A IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 GB/T 3077 12Cr2Ni4A IS 1570 (Part 4) 10Mo6 IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 4) 10Cr20Mo6 IS 4367 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H
Match Breakdown
CHEMISTRY MATCH
72.6%
MECHANICAL MATCH
0%
OVERALL
48.4%
Specifications
Property IS 1570 (Part 4) 40Cr13Mo10V2 IS 4367 10Cr9Mo10
Standard IS 1570 (Part 4):1988 IS 4367:1991
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 <=0.15
Si (%) 0.10-0.35 <=0.50
Mn (%) 0.40-0.70 0.40-0.70
Ni (%) <=0.30 <=0.30
Cr (%) 3.00-3.50 2.00-2.50
Mo (%) 0.90-1.10 0.90-1.10
V (%) 0.15-0.25 Not specified
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 40Cr13Mo10V2 IS 4367 10Cr9Mo10
Tensile Strength >=1540 MPa 410-590 MPa
Yield Strength >=1240 MPa (0.2 % proof stress) 245 MPa min
Elongation >=8% >=18%
Izod Impact >=14 J 55 J min
Hardness >=444 HBS (guidance only) Not specified
Condition Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 30 mm Normalised and tempered, ruling section up to 50 mm
Hardness (soft annealed) Not specified <=187 HB
Key Differences
Can IS 1570 (Part 4) 40Cr13Mo10V2 Be Substituted With IS 4367 10Cr9Mo10?
IS 1570 (Part 4) 40Cr13Mo10V2 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 4) 40Cr13Mo10V2
0 active listings and RFQs →
IS 4367 10Cr9Mo10
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 40Cr13Mo10V2 and IS 4367 10Cr9Mo10?
IS 1570 (Part 4) 40Cr13Mo10V2 specifies V which is not specified for IS 4367 10Cr9Mo10. IS 4367 10Cr9Mo10 specifies S, P which are not specified for IS 1570 (Part 4) 40Cr13Mo10V2.
Can IS 1570 (Part 4) 40Cr13Mo10V2 be substituted with IS 4367 10Cr9Mo10?
IS 1570 (Part 4) 40Cr13Mo10V2 and IS 4367 10Cr9Mo10 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.