IS 1570 (Part 4) 40Ni14 vs BS 970 (Part 1) 655H13

Related Material — 68.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 40Ni14 (IS 1570 (Part 4):1988) and BS 970 (Part 1) 655H13 (BS 970 (Part 1):1991) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 40Ni14 is defined under Bureau of Indian Standards (IS), originating from India, while BS 970 (Part 1) 655H13 is defined under British Standards (BS), originating from United Kingdom.

As per chemical composition, IS 1570 (Part 4) 40Ni14 vs BS 970 (Part 1) 655H13 is a 68.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a related material overall at 68.7%.

Frequently Compared With IS 1570 (Part 4) 40Ni14:
NF A35-565 100C6 IS 4367 07Cr4Mo6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 10Cr20Mo6 IS 1570 (Part 4) 10Mo6 IS 4367 10Cr9Mo10 IS 1570 (Part 7) 10Mo6H IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 7) 12Cr2Mo5V2H IS 11169 (Part 1) 10Ni5Cr4
Match Breakdown
CHEMISTRY MATCH
68.7%
MECHANICAL MATCH
No shared data
OVERALL
68.7%
Specifications
Property IS 1570 (Part 4) 40Ni14 BS 970 (Part 1) 655H13
Standard IS 1570 (Part 4):1988 BS 970 (Part 1):1991
Category Alloy Steel Alloy Steel
C (%) 0.35-0.45 0.10-0.16
Si (%) 0.10-0.35 Not specified
Mn (%) 0.50-0.80 0.35-0.60
Ni (%) 3.20-3.60 3.00-3.75
Cr (%) <=0.30 0.70-1.00
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 40Ni14 BS 970 (Part 1) 655H13
Tensile Strength 890-1040 MPa Not specified
Yield Strength >=650 MPa (0.2 % proof stress) Not specified
Elongation >=15% Not specified
Izod Impact >=55 J Not specified
Hardness 255-311 HBS (guidance only) Not specified
Condition Bars and forgings, hardened and tempered (oil hardened unless stated), limiting ruling section 63 mm Not specified
Typical Applications
IS 1570 (Part 4) 40Ni14
Not documented
BS 970 (Part 1) 655H13
Case hardening steel (section four)
Key Differences
Can IS 1570 (Part 4) 40Ni14 Be Substituted With BS 970 (Part 1) 655H13?
IS 1570 (Part 4) 40Ni14 and BS 970 (Part 1) 655H13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.
On M-EX Right Now
IS 1570 (Part 4) 40Ni14
0 active listings and RFQs →
BS 970 (Part 1) 655H13
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 40Ni14 and BS 970 (Part 1) 655H13?
IS 1570 (Part 4) 40Ni14 specifies Si which is not specified for BS 970 (Part 1) 655H13.
Can IS 1570 (Part 4) 40Ni14 be substituted with BS 970 (Part 1) 655H13?
IS 1570 (Part 4) 40Ni14 and BS 970 (Part 1) 655H13 share some compositional similarity but differ enough that substitution should not be assumed. Review the differences above carefully, and consult the applicable standard or a metallurgist before using one in place of the other.