IS 1570 (Part 4) 60Cr4V2 vs IS 5517 50Cr4V2

Close Alternative — 80.7% match based on chemical composition and mechanical property overlap.

IS 1570 (Part 4) 60Cr4V2 (IS 1570 (Part 4):1988) and IS 5517 50Cr4V2 (IS 5517:1993) are both steel grades. Both fall under the Alloy Steel category. IS 1570 (Part 4) 60Cr4V2 is defined under Bureau of Indian Standards (IS), originating from India, while IS 5517 50Cr4V2 is defined under Bureau of Indian Standards (IS), originating from India.

As per chemical composition, IS 1570 (Part 4) 60Cr4V2 vs IS 5517 50Cr4V2 is a 80.7% match. Mechanical property data is not available for both grades, so this factor could not be scored. Combined, this makes them a close alternative overall at 80.7%.

Frequently Compared With IS 1570 (Part 4) 60Cr4V2:
IS 1570 (Part 4) 07Cr4Mo6 IS 1570 (Part 7) 10Cr36Mo10H IS 4367 10Cr9Mo10 EN 10028-2 10CrMo9-10 IS 1570 (Part 4) 10Mo6 IS 4367 07Cr4Mo6 NF A35-565 100C6 UNI 11234 100Cr6 IS 1570 (Part 4) 103Cr4 IS 1570 (Part 4) 103Cr6 IS 1570 (Part 4) 105Cr5 IS 1570 (Part 4) 10Cr20Mo6
Match Breakdown
CHEMISTRY MATCH
80.7%
MECHANICAL MATCH
No shared data
OVERALL
80.7%
Specifications
Property IS 1570 (Part 4) 60Cr4V2 IS 5517 50Cr4V2
Standard IS 1570 (Part 4):1988 IS 5517:1993
Category Alloy Steel Alloy Steel
C (%) 0.55-0.65 0.45-0.55
Si (%) 0.10-0.35 0.15-0.40
Mn (%) 0.80-1.10 0.70-1.10
Cr (%) 0.90-1.20 0.90-1.20
V (%) >=0.15 0.10-0.20
S (%) Not specified <=0.035
P (%) Not specified <=0.035
Matched by chemical composition and mechanical properties, not a formal equivalence claim. Always verify against the applicable standard before substitution.
Mechanical Properties
Property IS 1570 (Part 4) 60Cr4V2 IS 5517 50Cr4V2
Tensile Strength Not specified 780-980 MPa
Yield Strength (0.2% proof) Not specified 590 MPa min
Elongation Not specified >=13%
Izod Impact Not specified 34 J min
Hardness (annealed) Not specified <=250 HB
Condition Not specified Hardened and tempered, ruling section up to 250 mm
Key Differences
Can IS 1570 (Part 4) 60Cr4V2 Be Substituted With IS 5517 50Cr4V2?
IS 1570 (Part 4) 60Cr4V2 and IS 5517 50Cr4V2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.
On M-EX Right Now
IS 1570 (Part 4) 60Cr4V2
0 active listings and RFQs →
IS 5517 50Cr4V2
0 active listings and RFQs →
Frequently Asked Questions
What is the difference between IS 1570 (Part 4) 60Cr4V2 and IS 5517 50Cr4V2?
IS 5517 50Cr4V2 specifies S, P which are not specified for IS 1570 (Part 4) 60Cr4V2.
Can IS 1570 (Part 4) 60Cr4V2 be substituted with IS 5517 50Cr4V2?
IS 1570 (Part 4) 60Cr4V2 and IS 5517 50Cr4V2 are a close alternative rather than a direct substitute. Some properties overlap well, but check the specific chemistry and mechanical rows above against your application's requirements before treating them as interchangeable.